Calcium Phosphate Cement Reinforced with Fiber

ZHAO Peng,LI Hong,ZHOU Chang-ren,SUN Tu-chun,LUO Bing-hong

DOI: https://doi.org/10.14136/j.cnki.issn1673-2812.2010.03.038

2010-01-01

Abstract:Calcium phosphate cement(CPC)sets to form hydroxyapatite and has been used in medical procedures.However,the brittleness and low strength of CPC limited its use in many stress-bearing locations.In the present study,a biodegradable PLLA(Ploy-L-lactic acid)nanofiber,which was prepared by spray-drying,was incorporated with CPC to reinforce its strength and fracture toughness.After having been combined with the PLLA fiber,the initial setting time of the CPC was shorter than that of unreinforced one;the main phase of the setting cement was the same hydroxyapatite as the unreinforced one.With increasing the nanofiber content from 0 to 15 wt%,the average compressive strength in wet of CPC increased from 4.13± 0.05 to 8.71±0.10MPa,and the fracture toughness in wet achieved an increment of 70%.Both strength and fracture toughness followed a fall at a nanofiber fraction of 20 wt%.Fractographic observation and crack propagation test revealed that this increase could be correlated to energy-dissipating processes along fiber and bridge effect of fiber.