Phase Transition in Ba6−3x(Sm1−yLay)6+2xTi18O54 (x=0.5) Ceramics

Ni Qin,Xiao Qiang Liu,Xiang Ming Chen

DOI: https://doi.org/10.1111/j.1551-2916.2006.01128.x

IF: 4.186

2006-01-01

Journal of the American Ceramic Society

Abstract:The effect of La substitution for Sm was investigated in Ba6−3x(Sm1−yLay)6+2xTi18O54 (x=0.5) ceramics in the entire range of y (0∼1.0). X‐ray diffraction (XRD) analysis indicated that the phase constitution of the present ceramics was sensitive to y, and an abnormal phase transition from the tungsten bronze‐type to a new Ba16Ce32Ti64O192‐type solid solution was determined at y=0.6–0.9. The crystal structure of the new phase was refined by Rietveld refinement. The stability of the Ba16Ce32Ti64O192‐type structure was discussed with the ordering of cations and the average radius of Ln3+. The Ba16Ce32Ti64O192‐type phase was observed only in the sintered pellets but not in the loose powders in the investigated temperature range of 1200°–1350°C. A differential scanning calorimetric analysis (DSC) was performed for investigating the thermal effect of the phase transition. Discontinuous dielectric properties were observed corresponding to the phase transition. The Ba16Ce32Ti64O192‐type phase has a much higher dielectric constant, a lower quality factor, and a larger positive temperature coefficient of resonant frequency at microwave frequencies in comparison with the tungsten bronze‐type phase. Besides, the dielectric loss of the Ba16Ce32Ti64O192‐type phase is much lower (tan δ∼10−4) at frequencies below 108 Hz, while the dielectric constant is insensitive to the frequency.