Abstract:This chapter focuses on the generation, development, inheritance and control of the defects in colloidal forming process, by which the complex near-net shape ceramic products with a homogeneous microstructure and high reliability were consequentially achieved.The rheological performance of the ceramics suspension was very important to the colloid forming processes. In our studies, the rheological behaviors of aqueous alumina suspensions were investigated, and the various ways of modifying the rheological behaviors of the suspensions were discussed. A critical solid loading between the shear thinning and shear thickening behavior was found in an aqueous alumina suspension. Moreover, the gelation of the suspension with high solid loading of alumina got delayed and the strength of green body decreased, which implies that the fast polymerization of monomers in high solid loading alumina suspension was inhibited, and the flexibility of the gel-casting was improved. We found that there was an optimal solid loading for the ZTA suspension to obtain the highest bending strength and the highest Weibull modulus for the sintered bodies.Micro mechanisms of agglomerations' generation in ceramic suspensions used in colloidal forming processing were investigated. On the basis of potential energy between particles in liquid, a microscopic model of agglomerations in ceramic suspensions was presented. Two types of agglomerations, tight agglomeration and loose agglomeration, were observed by using an environmental scanning microscope as a quasi-direct method. It is observed that their generation is caused by the deviation of solid phase content in slurry from the stable solid loading.The influences of the idle time on the microstructures and mechanical properties of green bodies were also described using direct coagulation casting. The vertically laminates cracks were observed in coagulated green bodies after casting using increasing ionic strength. The cracks were attributed to the shrinkage of the particle network (syneresis) during coagulation.The study indicated that the solid loading in the suspension depended on high valence counter-ions and ion conductivity constants. Further research revealed that the inner stress in the green bodies of ceramics originated from the non-uniform shrinkage during the solidification of the precursor suspension and the drying of the green bodies. The gradients of temperature, initiator concentration and moisture are the important original factors causing the inner stress.It is found that a proper amount of a water-soluble polymer, such as hydroxyethyl acrylate (HEA), polyethylene glycol (PEG) and poly (vinylpyrrolidone) (PVP) added into the concentrated suspension can adjust polymer network structure and thus reduce the inner stresses and cracking in the ceramic green body. The debindering time of large ceramic parts can be significantly shortened by reducing the harmful inner stresses in the green body.

Control of the inner stresses in ceramic green bodies formed by gelcasting

Research Progress in Improvement of the Gel System for Gelcasting Based on Defect's Controlling

A Study on Internal Stress of Slurry Solidification During Gelcasting

Origin, Transformation and Control of the Inner Stress in the Green Bodies Prepared by Ceramic Colloidal Forming Processing

Effects of Monomer Content on Internal Stresses During Solidification Process and Properties of Green Bodies by Gelcasting

Improvement of Microstructural Controllability of Cellular Ceramic for Multifunctional Composites

Generation, Development, Inheritance, and Control of the Defects During the Transformation from Suspension to Green Body

Natural additives in protein coagulation casting process for improved microstructural controllability of cellular ceramics

Suppression of Surface-Exfoliation by Gelcasting Ceramics with Mixed Polymer-Monomer Solutions

Recent Developments in Gelcasting of Ceramics

Study on mechanism for eliminating the surface flaws of green body prepared by gelcasting via polymer

Pretreatment Processing of Gelcast Green Body before Debinding

Improving the Homogeneity and Reliability of Ceramic Parts with Complex Shapes by Pressure-Assisted Gel-Casting

Gelcasting of alumina ceramics in the mixed acrylamide and polyacrylamide systems

Gas-discharging reactions and their effect on the microstructures of green bodies in gelcasting of non-oxide materials

Controllable Forming Technology in Gelcasting

Gelcasting of ceramic suspension in acrylamide/polyethylene glycol systems

Influence of the Compacts Homogeneity on the Incidence of Cracks During Thermal Debinding in Ceramic Injection Molding

Improved Gelcasting

Gas-discharging Reactions in Gelcasting of Si-containing Materials and Their Effect on Microstructure of Green Bodies

Study On Gel-Tape Casting In The Mixed Polyvinyl Alcohol And Acrylamide Systems