A Facile Cation-Exchange Strategy for ZnS-SnS-Sb<sub>2</sub>S<sub>3</sub>@C Submicron Box as Advanced Anode for Li-Ion Batteries
Miao-Ling Chen,Yi-Zhao Chen,Ling-Zhi Wang,Jing-Ru Cao,Xing-Wen Huang,Yue-Zhu Li,Rui-Bin Wang,Yi-Dong Liu,Jun-Qi Hu,Song-Yi Liao,Yong-Gang Min
DOI: https://doi.org/10.1002/cnma.202200540
IF: 3.82
2023-01-01
ChemNanoMat
Abstract:In this work, a hierarchical ZnS-SnS-Sb2S3@C (ZTAS@C) submicron box has been successfully prepared via a facile cation-exchange strategy and is used as advanced anode for Li-ion batteries. The composition and morphology of the as-prepared samples are measured by XRD, SEM and TEM, respectively. In addition, the as-synthesized hollow ZTAS@C architecture delivers a rate capability of 1001, 862, 765, 621, and 419 mAh g(-1) at 0.2, 0.5, 1.0, 2.0, and 4.0 A g(-1), respectively, and maintains reversible specific capacity of 581 mAh g(-1) after 100 cycles at 1.0 A g(-1) with the high CE value around almost 100%. Since 1 mol Sb2S3 could hold 4.8 times more Li+ ions than ZnS, the as-synthesized ZTAS@C delivers 2 similar to 3 times more specific capacity than the un-treated ZnS-SnS@C sample without cation-exchange during electrochemical testing. Moreover, the cycled ZTAS@C could maintain a relatively complete microscopic morphology of the submicron box with a lower electrode expansion rate of similar to 131%. Owing to synergistic effects between ZnS-SnS-Sb2S3, such as stable structure from ZnS, faster ionic conductivity from SnS and higher capacity from Sb2S3 (theoretically 947 mAh/g), ZTAS@C anode showed excellent electrochemical enhancements as using for LIBs anode. Therefore, the cation exchange strategy should be a facile way to improve the rate performance and cycle stability of multi-metals sulfide composites.