Abstract:Decomposition of SmBa2Cu3Ox (Sm-123) films deposited on MgO substrates was in situ observed by high-temperature optical microscopy. The films were detected to be predominantly c-axis oriented, with highly fourfold symmetry. It was observed that a minor change in the a-axis-oriented grains percentage had a strong effect on the thermal stability of the films and the melting mode. In the case of nearly 1% of a-oriented grains, the decomposition temperature of the SmBCO film was above the peritectic temperature (T-p), showing a high thermal stability. The peritectic product of the Sm2BaCuO5 (Sm-211) phase exhibited the preferential orientation of [0 0 1] parallel to [1 1 0] of the Sm-123 matrix. On the other hand, when substitution of a-axis-oriented grains increased up to 3% or more, the decomposition temperature of the Sm-123 film dropped below T-p. Interestingly, in the latter case, the Sm-211 phase had an epitaxial relation with Sm-123 as Sm-211[0 0 1]//Sm-123 [1 0 0] or Sm-211[0 0 1]//Sm-123[0 1 0], distinctly different from that mentioned above. In this paper the melting behaviour and its mechanisms, together with the epitaxial orientation of Sm-211 grains in Sm-123 thin films, are studied in detail by means of the interface-energy analysis.

Real-Time Observation of Growth and Orientation of Sm-Ba-Cu-O Phases on A Sm-211 Whisker Substrate by High-Temperature Optical Microscopy

In Situ Study of Sm–Ba–Cu–O Phases Formation on and Epitaxial Relations with Sm211 Whisker by High-Temperature Optical Microscopy

Re123 Epitaxial Growth on Sm211 Whiskers

The Qualitative Change in Decomposition of C-Oriented Sm-123 Films Due to A Minor Change in Substitution of A-Oriented Grains

Preferential Growth of Smbco on Sm211 Whiskers and Its Dependence Upon Supersaturation

On The Thermal-Instability Of Crystal Bi2sr2cuox (2201)

Growth mechanism of SmBaCuO crystal fiber

Crystal Growth of A High-T-C Smbco Superconductor in 1 Atm Oxygen Pressure

Observation of a Surface Alloying-to-dealloying Transition During Growth of Bi on Ag(111)

Crystal Growth And Phase Relation Of Sm1+Xba2-Xcu3oz

Growth of Y<sub>1</sub>Ba<sub>2</sub>Cu<sub>3</sub>O<sub><i>x</i></sub>Single-Crystal Whisker Using Sb-doped Precursor

Real-time observation of the melting process of YBCO thin film on MgO substrate

A New Growth Technique of Ca-Free&lt;tex&gt;$rm Y_1rm Ba_2rm Cu_3rm O_rm X$&lt;/tex&gt;single-Crystal Whiskers Using Antimony-Doped Precursors

A Study on the In-Situ Growth of Highly Oriented Zno Whisker

Growth of A High Performance Smbco Bulk Superconductor with the Addition of A Sm2ba4cu2o9 Phase

Phase Decomposition and Superconductivity in Bi2Sr2CaCu2Oy Single Crystals

Twinning microstructure in the solid-phase epitaxial crystallization of BaTiO3

Formation and Characterization of YBa2Cu3O7−δ High-Tc Thin Films by MOCVD with Single Mixed Precursor

A New Growth Technique Of Ca-Free Y1ba2cu3ox Single-Crystal Whiskers Using Antimony-Doped Precursors

Growth and Anisotropic Properties of RBa_2Cu_3O_x Single-Crystal Whiskers

The Microscopic Study of Y-Ba-Cu-O Compound