Abstract:The particle size and pore size of spherical mesoporous silica materials play significant roles in their application. However, relatively limited systematic research has been conducted on how preparation conditions influence these properties. In particular, the effects of some important factors have not been adequately studied, including reaction time, reaction temperature, and organic solvent type. In this work, octane and water were used as solvents, and tetraethyl orthosilicate was used as the silicon source to systematically study the effects of reaction time, reaction temperature, different organic solvents, octane/water mass ratio, styrene template concentration, and surfactant (cetyltrimethylammonium bromide, CTAB)/H2O mass ratio on the particle morphology, particle size, and pore size of silica. The results suggest that the above-mentioned neglected factors exert a substantial influence on both particle size and pore size. In the experimental temperature range, the pore diameter decreases and the particle size increases with increasing temperature. The maximum particle size and pore size are achieved after a reaction time of 3 h, and a further increase in reaction time leads to a smaller particle size and pore size. As the number of carbon atoms in the organic solvent decreases, the pore size also gradually increases. Styrene and organic solvents that dissolve in CTAB micelles are crucial factors in pore formation, while the aggregation of the swollen CTAB micelles influences the particle size. The changes in the pore structure stability and hydroxyl density of the synthesized samples in water were also studied. After undergoing water treatment at temperatures ranging from 20 to 60 °C for 72 h, both the pore structure and morphology remain relatively unchanged. When the temperature increases, the surface hydroxyl density exhibits a more pronounced increase in the presence of water. After water treatment for 5 h, the surface hydroxyl density reaches saturation.

Synthesis of the Polymethylsiloxane Microspheres in Micron Size

Microdroplet-based Synthesis of Polymethylsilsesquioxane Microspheres with Controllable Size, Surface Morphology, and Internal Structure

Synthesis of Poly(styrene-Co-3-trimethoxysilyl Propyl Methacrylate) Microspheres Coated with Polysiloxane Layer

Synthesis and Characterization of Polymethylsilsesqui Oxane Microspheres by the Two-Step Sol-Gel Method

Preparation and Characterization of Micron-Sized Hollow Polysiloxane Spheres

Size-Controlled Synthesis of Monodispersed Poly(3-mercaptopropylsilsesquioxane) Microspheres by a Two-Step Sol–Gel Method

Facile Synthesis of Micron-Sized Thiol-Functional Polysilsesquioxane Microspheres Through a One-Step Sol-Gel Method

Continuous-flow Synthesis of Polymethylsilsesquioxane Spheres in a Microreaction System

Micron-Sized Thiol-Functional Polysilsesquioxane Microspheres with Open and Interconnected Macropores: Effects of the System Composition on the Porous Structure and Particle Size of the Microspheres

Preparation and characterization of micron-sized polystyrene/polysiloxane core/shell particles

Preparation and Characterization of Polysilsesquioxane Microspheres with Different Organofunctional Groups

Effects of synthesis conditions on particle size and pore size of spherical mesoporous silica

Systhesis of Monodispersed Silica Microspheres and the Formation Mechanism

Mini-Emulsification and Mini-Emulsion Polymerization of Methyl Methacrylate/Nanosilica Dipsersion

Formation Mechanism of Monodispersed Polysilsesquioxane Spheres in One-Step Sol-Gel Method

Preparation and Formation Mechanism of Narrow-Dispersed Poly(Aminopropyl/Phenylsilsesquioxane) Microspheres

Preparation of silica micro spheres via a semibatch sol–gel method

Synthesis of monodispersed mesoporous silica spheres (MMSSs) with controlled particle size using gemini surfactant

Synthesis of micrometer-sized hard silica spheres with uniform mesopore size and textural pores

Micron-Sized Thiol-Functional Polysilsesquioxane Microspheres with Open and Interconnected Macropores: Preparation, Characterization and Formation Mechanism

Preparation of silica microspheres by hydrolysis of silicon tetrachloride in microemulsion