Abstract:Concrete-to-concrete interfaces present both in new and existing construction, are commonly regarded as the weak link. Durability research of interfaces is a vital prerequisite for structural rehabilitation and strengthening applications under marine and coastal environments. Hence, to clarify the chloride ion transport behavior be-tween the new-old concrete composite system and its constituents, microstructural characteristics of the in-terfaces with various preparation methods were determined via field emission scanning electron microscopy. Then, the time-dependent diffusion chloride ion penetration together with its steady-state concentration distri-bution evaluated by using AgNO3 chromogenic, electron microprobe, and energy spectrum methods, as well as the numerical simulation based on the real interface roughness from the 3D laser scanning optical system. Results show that microcracks and a large amount of CaCO3 precipitations were formed in the concrete-to-concrete interface, where its porosity was higher compared to that of the matrix and interface transition zone around coarse aggregate; Therefore, the interface regions have higher tortuosity of water transport channel and strengthen the solution absorption rate, resulting in the internal chloride ions not only diffuse deeper perpen-dicular to the exposed surface but also ingress into the concrete on both sides as the concentration gradient simultaneously, leading to a "diffusion peak" formation. Furthermore, the effects of groove characteristics (such as orientations, clearance, width, and depth) on chloride transport were modeling evaluated in this study, in which the interfacial relationship could be optimized setting the reasonable groove and achieving the goal of durability equivalent to the cast-in-place structure.

INFLUENCE OF SELF-HEALING ON CHLORIDE ION INGRESS IN CRACKED CONCRETE

Investigating the Self-Healing Performance of Cracked Undersea Constructions

Experiments of chloride ingression in flexural reinforced concrete beams

Influence of Flexural Loading on Chloride Ingress in Concrete Subjected to Cyclic Drying-Wetting Condition

InfIuence of Ioad crack on chIoride diffusion in concrete

Chloride Penetration into Concrete Damaged by Uniaxial Tensile Fatigue Loading

Influence of cracking on chloride diffusivity and moisture influential depth in concrete subjected to simulated environmental conditions

Modeling of chloride ions diffusion in cracked concrete

Model of Chloride Penetration into Cracked Concrete Subject to Drying–wetting Cycles

Interactions between Organic Chelation Agents and Ions in Seawater for Accelerating Self-Healing of Cracks in Cement Paste

Experimental study on electrical characteristics of ions in concrete at early age under electric field

A new self-healing agent for accelerating the healing kinetics while simultaneously binding seawater ions in cracked cement paste

Assessment of self-healing performance of cement-based materials incorporating ion chelator and industrial wastes

The self-healing of marine concrete cracks based on the synergistic effect of microorganisms and inorganic minerals

Experimental and Numerical Study on the Microstructure and Chloride Ion Transport Behavior of Concrete-to-concrete Interface

Investigation into the Effects of Crystalline Admixtures and Coatings on the Properties of Self-Healing Concrete

Chloride ingression in cracked concrete under saturated state

The Effect of Crack Width on Chloride-Induced Corrosion of Steel in Concrete

INFLUENCE OF CRACKING WIDTH TO CONCRETE DURABILITY

Effect of Cracks in Concrete on Chloride Penetration

Effect of Chloride Removal and Corrosion Prevention for Cracked Concrete Based on Bi-Directional Electro-Migration Rehabilitation