Abstract:In the article, electrochromic WO 3 films were obtained from 25, 100, and 200 mM peroxytungstic acid (PTA) solution. A chronoamperogram of the cathodic reduction of tungsten oxide (WO 3 ) through the stages of formation of a precursor film adsorbed on the surface of the ITO electrode and its subsequent staged reduction to WO 3 and side formation of soluble reaction products is presented. The material yield of the WO 3 film on ITO glass was within 50%, which is due to the parallel occurrence of side processes associated with hydrogen evolution and the reduction of tungsten complexes that were in the precipitation solution (WO 3 reduction scheme). In this case, it was taken into account that thin WO 3 films were the final product. The features of the synthesis of peroxytungstic acid have been studied. It has been shown that the reaction of W dissolution in 37% H 2 O 2 proceeds exothermically. In this case, the reaction temperature reached 96°C within a few seconds, and its decline varied exponentially with the formation of reaction products. The dependence of the limiting current on the square root is obtained. The presented graphic dependence is characterized by linearity, while the beginning of the straight line does not coincide with the origin. The process of intercalation-deintercalation of protons (H + ) (cathode-anode branches of CV) was a consequence of structural and reversible changes as a result of H + intercalation. WO 3 films obtained by electrochemical (cathodic) deposition can be recommended as an electrode material for electrochromic devices (cathode) and as a material for electrochemical sensors. Another promising direction is the development of a wide band gap anode based on WO 3 for photovoltaic devices, which are energy efficient hydrogen generation systems.

Electrochromism of Electrodeposited Tungsten Trioxide Films: I . Electrochemical Characterization

Electrochromism of titanium oxide thin films

Quasi–symmetric Electrochromic Device with two kinds of Amorphous Tungsten Oxide Films

Enhanced electrochromism from non-stoichiometric electrodeposited tungsten oxide thin films

Electrochromic property of tungsten trioxide films prepared by DC magnetron sputtering with oblique angle deposition and thermal oxidation

Optical Characterization of the Coloration Process in Electrochromic Amorphous and Crystalline Wo3 Films by Spectroscopic Ellipsometry

Electrochromic composites films composed of MoO 3 doped by tungsten atoms with remarkable response speed and color rendering efficiency via electrochemical deposition

Electrochromic switching of tungsten oxide films grown by reactive ion-beam sputter deposition

Citric Acid Induced W18O49 Electrochromic Films with Enhanced Optical Modulation

Preparation and properties of all solid-state electrochromic devices based on tungsten oxide nanocomposites

The Performance of Electrochromic Tungsten Trioxide Films Doped with Cobalt or Nickel

Improved Electrochromic Performance of WO3 Films with Size Controlled Nanorods

Regularities of Obtaining Electrochromic WO3 Films at the Cathode Polarization of the Electrode

Effect of In Situ Heating on the Growth and Electrochromic Properties of Tungsten Trioxide Thin Films

Rapid and low-temperature preparation of tungsten oxide electrochromic thin films by oxygen plasma treatment

Electrochromic Properties of Nano-columnar Porous WO<sub>3-x</sub>/TiO<sub>2</sub> Thin Films

Electrochromism of Nanocrystal-in-Glass Tungsten Oxide Thin Films under Various Conduction Cations

Pseudocapacitive Charge Storage in Electrochromic Transition-Metal Oxide Thin Films

Electrochromic Device with A Polymer Ionic Conductor

Enhancement of electrochromic properties using nanostructured amorphous tungsten trioxide thin films

Enhanced electrochromic and mechanical properties of WO 3 film by substrate effect