Qantitative Pattern of the Change in Microstructure and Surface Properties of Electric Ceramic During Sintering Processes
Kan YANG,Xian-cai LU,Xian-dong LIU,Zhi-jun LU,Yu-long LI,Lian-ze ZHAO,Hai-long CAI
DOI: https://doi.org/10.3969/j.issn.1001-1625.2007.02.003
2007-01-01
Abstract:Sintering process directly influences the specific surface area,microstructure,pore size distribution and other interface properties of the ceramic,which influence its material characteristics and practical performance crucially.In this paper,the changes in surface and interface properties and pore structure of the electric ceramic for power-transmission equipments during high strength sintering process were studied systematically.Original sample and five of different sintering temperatures were prepared and their N2 adsorption-desorption isotherms were measured.Based on the adsorption and desorption data,the specific surface area,pore volume,pore size distribution by BJH method and surface fractal dimension by FHH method were calculated.In addition,the microstructures of these samples were observed using scanning electronic microscopy.Furthermore,the coincidence relation between the observed phenomena and sintering temperature was discussed.Results show that specific surface area,pore volume and surface fractal dimension are nearly not changed before 700℃.At 1000℃,surface fractal dimension reaches the summit value,while the specific surface area and pore volume decrease sharply at 1340℃.Combined with the SEM observation results,it is indicated that these changes are directly related to the dehydration,mineral phase transformation,movement of crystal boundaries and the growing of crystal grain.