Abstract:With increasing requirements for environmental protection and energy conservation, Al–Cu powder alloys play an important role in machine weight reduction. During the preparation of the Al–Cu powder alloy, an appropriate sintering temperature helps improve the comprehensive performance of the alloys. In this study, powder metallurgy was used to prepare Al–7.5Cu–1Si alloys, and the effects of different sintering temperatures on their relative sintering density, hardness, and tensile strength were studied. The microstructure and phase composition of the alloy were observed and analyzed by scanning electron microscopy and X-ray diffraction, and the mechanical properties of the alloy were studied using a Brinell hardness tester and a universal material testing machine. By analyzing the microstructural changes of the alloys at different sintering temperatures, the optimal sintering temperature of the alloy was determined to obtain the best properties. The results demonstrated that the sintering temperature significantly affected the diffusion and migration of the metal particles inside the alloy. When the temperature was low, numerous pores were present in the alloy, and the degree of bonding between the metal particles was poor. As the temperature increased, the number of pores in the alloy decreased, and good metallurgical bonding occurred between the particles. The relative densities and mechanical properties of the alloys were significantly affected by the sintering temperature. When the temperature was below 570 °C, the relative density and mechanical properties were low. At 590 °C, the alloy underwent deformation and was in an over-sintered state. The best sintering temperature was 570 °C. This is because at this temperature, the relative sintering density, hardness, and tensile strength of the alloy all reached maximum values, which were 98.6%, 71 HB, and 153 MPa, respectively.

STUDY ON SINTERING PROCESS OF Al- 10mg BINARY ALLOY SYSTEM

STUDY ON SINTERING PROCESS OF ALLOYS OF Al-Zn AND Al-Cu BINARY SYSTEMS

THE EFFECT OF HEATING METHOD TO SINTERING PROCESS OF PURE METAL POWDERS

Investigation of a Hot-Pressed Nb–Ti–Al Alloy: Mechanical Alloying, Microstructure and Mechanical Property

In-situ Observation on Sintering Process of Al-Cu Alloy

Study of Hot-press Sintering Process of Nanometer Cu-Al_2O_3 Composite

The Effect of Solution Treatment on the Si Particles’ Morphology Evolution and the Thermal Conductivity and Tensile Properties of Sb-Modified Al-8Si-0.6Mg Alloys

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Effects of sintering time on the microstructure and properties of an Al-Cu-Mg alloy

Effect of Stored Energy on Sintering Process of Pure Metal Powders

Effect of fluctuating temperature field on the sintering of Al–10Mg alloy

Microstructure, Mechanical Property and Thermal Conductivity of Al–Si–Fe–Mg Alloy Solidified under High Pressures

Synthesis of Tial Based Alloy by Mechanical Milling, Warm Pressing and Reactive Sintering

Effect of sintering temperature on the microstructure and properties of Al-7.5Cu-1Si alloy

Study on Thermal Conductivity of Si3N4 Sintered with Y2O3-MgO Additive System

Investigation on microstructure and properties of Ti-45Al-5.5(Cr, Nb, B, Ta) alloy prepared by double mechanical milling (DMM) and spark plasma

Effect of Temperature-Related Factors on Densification, Microstructure and Mechanical Properties of Powder Metallurgy TiAl-based Alloys

An Improved Process for Solving the Sintering Problem of Al-Si Alloy Powder Metallurgy

Effect of Heat Treatment on Microstructure and Properties of Selective Laser Melting AlSi10Mg Alloy

Effect of cooling rates and heat treatment time on Si phase of AlSi10Mg alloy manufactured by selective laser melting: Microstructure evolution and strengthening mechanism

Effect of Processing Parameters on Tensile Properties and Microstructure of Selective Laser Melted AlSi10Mg Alloy