The Preparation of Polyethylene/Collagen Composites by Using Reactive Compatibilization Process
ZHOU Guo-quan,JIANG Lan,SHAO Shuang-xi,LUO Neng-zhen,XIANG Xian-gao,XU Yi-ming,Xinzhi Chen
DOI: https://doi.org/10.3969/j.issn.1003-9015.2013.04.021
2013-01-01
Abstract:The polyethylene/collagen based composites with good mechanical properties were prepared by using dicumyl peroxide as initiator,ethylene acrylic acid copolymer(EAA) and polyethylene-graft-maleic anhydride(PE-g-MAH) as compatibilizer,respectively.The influence of preparation process,the amount of compatibilizer,and the amount of collagen on the composite properties were studied in details.The results show that:(1) The process of reactive compatibilization by using twin screw extrusion is better than others;(2) The polyethylene/collagen composites reach the optimal mechanical properties when the PE-g-MAH was used as compatibilizer and the weight ratio of PE/collagen/ PE-g-MAH is 100:15:15,the elongation,tensile strength and impact strength are 88.6%,12.5 MPa and 26.7 kJ·m-2,respectively;(3) The polyethylene/collagen composites reach the optimal mechanical properties when the EAA was used as compatibilizer and the weight ratio of PE/collagen/EAA is 100:15:20,the elongation,tensile strength and impact strength are 90.5%,11.8 MPa and 21.5 kJ·m-2,respectively.