Abstract:Self-organized TiO2 nanotube arrays with micro-scale length were prepared on fluorine-doped tin oxide (FTO) conducting glass in NH4F/glycerol electrolyte by electrochemical anodization of pure titanium films deposited by radio frequency magnetron sputtering (RFMS) at room temperature. The samples were characterized by means of field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), and photoelectrochemistry methods. The results showed that Ti films prepared at the condition of Ar pressure 0.5 Pa, power 150 W, and 0.5 h at room temperature possessed the zone T model structure with good homogeneity and high denseness. When the anodization time was prolonged from 1 to 3 h at the voltage of 30 V, the pore diameter of TiO2 nanotubes increased from 50 to 75 nm, and the length increased from 750 to 1100 nm and then gradually decreased to 800 nm, while their wall morphology changed from smooth to rough. Also with increasing the anodization voltage, the pore diameter became larger, and the remaining oxide layer reduced, which could be easily removed by ultrasonic-chemical cleaning in 0.05% (w, mass fraction) diluted HF solution. Moreover, the photocurrent response curves and electrochemical impedance spectroscopy (EIS) results indicated that UV-illumination clearly enhanced the effective separation of the electron-hole pairs and the crystallized electrodes from the annealing treatment of as-anodized electrodes at 450 °C exhibited a better photoelectrochemical performance.

Preparation of High-Orderly Tio2 Nanotubes in Organic Solution and Characterization of C-Doped Tio2

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

PREPARATION OF HIGH-ORDERLY TIO2 NANOTUBES IN DIFFERENT CONDITIONS AND ELECTROLYTE SOLUTIONS

Preparation and Characterization of N-Doped TiO_2 Nanotube

Preparation and Photocatalysis Property of N Doped TiO_2 Nanotube

Preparation of High-ordered TiO2 Nanotube Arrays

One-step preparation of C-doped TiO<sub>2</sub> nanotubes with enhanced photocatalytic activity by a water-assisted method

Fabrication of highly ordered titanium dioxide nanotube array and investigation of its photocatalytic activity

Preparation and Characterization of TiO2 Nanotube Arrays Via Anodization of Titanium Films Deposited on FTO Conducting Glass at Room Temperature

Fabrication and Properties of Tio2 Nanotube Arrays Using Glycerol-Dmso-H2o Electrolyte

Synthesis and investigation of TiO2 nanotube arrays prepared by anodization and their photocatalytic activity

Preparation and Characterization of TiO<SUB>2</SUB> Nanotube Arrays by Anodic Oxidation Method: Preparation and Characterization of TiO<SUB>2</SUB> Nanotube Arrays by Anodic Oxidation Method

Preparation and characterization of the highly regular nitrogen doped anatase TiO2 nanotube

Progress of TiO_2 Nanotubes Prepared by Anodic Oxidation Method and Their Photocatalysis

Fabrication and Property Investigation of the Highly Ordered TiO2 Nanotube Arrays

Study on Synthesis in Situ and Photocatalytic Activity of Tio2 Nanotubes Array Films

Anodization Fabrication of Highly Ordered Tio2 Nanotubes

Preparation Of Tio2 Nanotube Arrays And Their Photoeleetrochemical Properties

Controllable Synthesis of Well-Ordered TiO2 Nanotubes in a Mixed Organic Electrolyte for High-Efficiency Photocatalysis

Structural Manipulation of the Photocatalytic Activity of Tio2 Nanotube Arrays