Abstract:Herein, α-GaOOH micro/nanorods were synthesized by facile template free hydrothermal methods. These rods were converted as mesoporous β-Ga2O3 nanostructures via thermal annealing at 900 °C for 2 h. The structural analysis (XRD) reveals the presence of orthorhombic (α-GaOOH) and monoclinic (β-Ga2O3) phases (pre- and post-annealing). The surface morphology, shape, size and porous structure, growth direction and crystalline quality of the micro/nanorods are investigated using scanning and transmission electron microscopy. Interplanar spacing of 0.37 and 0.46 nm confirms that the growth is along (2 0 1) and (−2 0 1) plane, respectively. The possible growth mechanism was proposed based on the obtained micro-graphical analyses. EDX, elemental mapping and XPS analyses revealed the existence of Ga and O and their chemical states. The characteristic Raman phonon modes confirmed the monoclinic phase of β-Ga2O3. The optical absorbance edge varies between 231 nm (GaOOH) to 290 nm (β-Ga2O3). Subsequently, the band gap varies between 5.6 and 4.4 eV. PL result showed intense ultraviolet and less intense violet-blue emissions, which can be related to the defect level emission. The BET surface area analysis confirmed the mesoporous structure with pore diameter (3.97 nm) and high specific surface area (13.87 m2/g) of Ga-3. The 98 % degradation efficiency with reaction kinetic rates of k = 0.0144/min shows a good catalytic behaviour of Ga-3 catalyst against RhB dye. The results reveal that the hydrothermally grown 1-D β-Ga2O3 mesoporous nanostructures are promising candidates for designing a catalytic and other functional nanodevices.

Novel Nanostructures of Β-Ga2o3 Synthesized by Thermal Evaporation

β-Ga2O3 Nanostructures: Chemical Vapor Deposition Growth Using Thermally Dewetted Au Nanoparticles as Catalyst and Characterization

Large Well-Aligned Nanostructures Of Beta-Ga2o3 Synthesized By Microwave Plasma Chemical Vapor Deposition

MgO nanostructures synthesized by thermal evaporation

Facile Synthesis and Characterization of Β-Ga[sub 2]o[sub 3] Nanostructures Via Vapor Transport Method

Synthesis of Single-Crystalline ?-Ga2o3 Nanoribbons

A simple method to synthesize gallium oxide nanosheets and nanobelts

Synthesis of β-Ga2O3 nanowires through microwave plasma chemical vapor deposition

Facile Synthesis And Characterization Of Gallium Oxide (Beta-Ga2o3) 1d Nanostructures: Nanowires, Nanoribbons, And Nanosheets

Catalyst-free Growth of Β-Ga2o3 Microstructures by Thermal Oxidation

Ga2O3 nanowires prepared by physical evaporation

Synthesis, phase conversion and physical characteristics of mesoporous β-Ga2O3 nanostructures for catalytic applications

Synthesis of beta-gallium oxide nanobelts through microwave plasma chemical vapor deposition

Effect of Ga on the Morphology of SnO 2 Nano/Micro-Crystals Grown by a Thermal Evaporation Method

Direct synthesis of beta gallium oxide nanowires, nanobelts, nanosheets and nanograsses by microwave plasma

One-dimensional Silicon Nanostructures Fabricated by Thermal Evaporation

Preparation, characterization and formation mechanism of gallium oxide nanowires

Catalyst-assisted heteroepitaxial strategy for highly ordered β-Ga 2 O 3 nanoarrays and their optical property investigation

Controllable Synthesis of SnO2 Nanowires and Nanobelts by Ga Catalysts

Controllable Ga/Ga 2 O 3 Nanowire Growth at High Temperatures Enabled by Au and Pd Quantum Dot Catalysts

Comparative Study of Growth Morphologies of Ga2O3 Nanowires on Different Substrates