Abstract:On a composite surfactant template(Brij35 and PEG), ordered mesoporous TiO2 was synthesized successfully. The formation of the ordered mesoporous TiO2 was analyzed by continuously monitoring the conductivity and viscosity during the reaction process, the ordered mesoporous TiO2 formed was characterized by XRD, HRTEM, SEM, FT-IR and N-2 adsorption and desorption methods. The results indicated that ordered mesoporous TiO2 was of a hexagonal packed structure, at a temperature below 400 degreesC, ordered mesoporous TiO2 has a higher thermal stability and a higher surface area of 252 m(2) (.) g(-1), the mesoporous pore diameter was uniform with a value of 3.4 nm and the crystal was in anatase phase. After TiO2 was calcined at 500 degreesC, ordered mesoporous structure was destroyed somewhat, and the formation of rutile phase appeared. The results also showed that liquid crystal template played a key role for the reaction, especially in a high polar media, in which non-polar carbon-hydrogen chain easily coagulated forming micelle, and TBOT gathered around the micelle formed, when they were acted by acid, reaction took place gradually to generate ordered mesoporous structure TiO2. It was found that taking efficient measures to control the hydrolysis and condensation processes of the reaction was the key of forming ordered mesoporous structure TiO2.

Formation of Orderly Organized Cubic Pbs Nanoparticles Domain in the Presence of Tio2

Surface Synthesis of PbS Nanoparticles on Silica Spheres by a Sonochemical Approach

High Yield Synthesis of PbS Nanocubes Using One-Step Solid-State Reaction in the Presence of an Anionic Surfactant

Synthesis and evolution of PbS nanocrystals through a surfactant-assisted solvothermal route.

Structure and Morphology of Nanosized Pbs on Tio2 Nanoporous Film in Dye-Sensitized Solar Cells

Nanostructured Lead Sulfide Containing Nanoholes Templated by Lyotropic Hexagonal Liquid Crystals

Preparation of rod-shape PbSO4 nanocrystal and its phase transition to PbS

Hydrothermal Preparation of Uniform Cubic-Shaped Pbs Nanocrystals

Hydrothermal preparation of one-dimensional assemblies of PbS nanoparticles

Preparation of SiO 2 /tio 2 Janus Particles by Electrostatic Assembly,hydrolysis and Calcination

Buildup Of Composite Films Containing Tio2/Pbs Nanoparticles And Polyelectrolytes Based On Electrostatic Interaction

Morphology Control of Nanoscale PbS Particles in a Polyol Process

Shape-Controlled Syntheses of Pbs Submicro-/Nano-Crystals Via Hydrothermal Method

Preparation, Optical Spectroscopy, And Electrochemical Studies Of Novel Pi-Conjugated Polymer-Protected Stable Pbs Colloidal Nanoparticles In A Nonaqueous Solution

Preparation and characterization of quantum-sized pbs grown in amphiphilic oligomer Langmuir-Blodgett monolayers

Synthesis of Ordered Mesoporous TiO<sub>2</sub> on a Composite Surfactant Template

Morphology Control of Pbs Nanocrystals by A Novel Hydrothermal Process

Formation of Ag Nanoparticles in Percolative Ag–PbTiO3 Composite Thin Films Through Lead-Rich Ag–Pb Alloy Particles Formed As Transitional Phase

The synthesis of hydrophobic nano-TiO2 powder and its photocatalytic property

Hierarchical, Star-Shaped Pbs Crystals Formed by A Simple Solution Route

Sub-10 nm monodisperse PbS cubes by post-synthesis shape engineering.