Microstructure and Performance of Tungsten Coatings Prepared by Low Pressure Plasma Spraying

杨震晓,刘敏,邓春明,陈明娟,邓畅光,车晓舟

DOI: https://doi.org/10.16577/j.cnki.42-1215/tb.2013.02.010

2013-01-01

Abstract:W coatings with thickness of 0.9～1.2 mm were fabricated on CuCrZr substrate by low pressure plasma spraying(LPPS) while four sets of spraying parameters were adopted.The microstructure,oxygen content and thermal conductivity of assprayed W coatings were analyzed with a scanning electron microscope,an oxygen and nitrogen analyzer,and a flashlight heat conducting meter.The pore size distribution of the W coatings prepared under the optimized spraying parameters was determined,and the effects of spraying power and vacuum chamber pressure on the microstructure and performance of assprayed W coatings were investigated.It was found that the four kinds of assprayed W coatings all had laminar structure,and the W coating obtained under the optimized spraying parameters had a compactness of 98.4%,an oxygen content of 0.2%(mass fraction),a thermal conductivity of 110.76 W/(m·K),and a pore size distribution of 0.2~4.0 μm(the dominant pore size was about 1.0 μm).