Microstructure, mechanical properties, and cavitation erosion performances of cold sprayed CuZn35 coatings
Pengyuan Diao,Fang Wang,Xin Chu,Yu Long,Yingchun Xie,Chunming Deng,Guosheng Huang,Min Liu,Zexin Yu
DOI: https://doi.org/10.1016/j.surfcoat.2022.129074
IF: 4.865
2022-11-19
Surface and Coatings Technology
Abstract:CuZn alloy (as known as brass) is widely used in ship components due to its combination of high hardness and fatigue strength, and therefore good cavitation erosion performance. In this study, CuZn35 powder was for the first-time cold spray deposited on pure aluminum substrates for potential application as cavitation protection of hull pipelines. Parametric studies were carried out and the respective deposition characteristics were analyzed, and cavitation erosion performances of different CuZn35 coatings were characterized in deionized water using ultrasonic vibration experiments. The results showed that with the increase of gas temperature, cold sprayed CuZn35 coatings generally showed better cold sprayability and coating performance on aluminum substrates. The cold sprayed CuZn35 coatings exhibited a dense structure (porosity ~0.43 %), fine grain (~0.549 μm), a relatively high microhardness (~226 HV), and a relatively high bonding strength (54 MPa). The cavitation resistance of cold sprayed CuZn35 coatings showed a lowest volume loss rate of 0.22 mm 3 /h in deionized water, which was lower than that of as-cast CuZn35 (0.39 mm 3 /h). After 120 min cavitation, various features such as undulation deformation, pit and crack propagation, and material peeling appeared on cold sprayed CuZn35 coatings. It was noted that cold sprayed CuZn35 coatings, different from the as-cast CuZn35, exhibited the main cavitation mechanism of delamination caused by interlayer crack propagation.
physics, applied,materials science, coatings & films