Abstract:The copper-cerium composite oxides supported on silicon carbide (SiC) catalysts (CuO-CeO2/SiC) for sulfuric acid decomposition were studied in sulfur-iodine (SI or IS) cycle. The influence of calcination temperatures (800 degrees C-1000 degrees C) of CuO-CeO2/SiC catalysts on their activities and morphology were investigated in this study. The activity of CuO-CeO2/SiC was prominently higher than that of CuO-CeO2 composite oxides catalyst. The SO3 conversion ratio of CuO-CeO2/SiC catalyst increased with calcination temperature from 800 degrees C to 900 degrees C, while decreased with calcination temperature at 900 degrees C-1000 degrees C. XRD pattern, TEM (HRTEM) images and Energy Dispersive X-ray (EDX) spectra revealed that copper-cerium composite oxides were well dispersed and immobilized on the surface of SiC grains. XRD pattern showed that the accelerated transformation of SiC crystals to amorphous SiO2 and the rapid expansion of CeO2 sub-grains at the calcination temperature of 900 degrees C-1000 degrees C, as well as the accelerated amorphization of CuO crystals at 800 degrees C-900 degrees C. The agglomeration of catalysts with sintering temperature was also proven by the BET test. At a higher calcination temperature, X-ray photoelectron spectroscopy (XPS) of Cu-2p spectra revealed the reduction of more Cu2+ in the process of SiC oxidation. According to TEM (HRTEM), XPS, and infrared radiation, the amorphous SiO2 was produced by the oxidation of superficial SiC particles, and the thickness of the SiO2 layers on SiC grains increased with the calcination temperature. A simple mechanism depicted the oxidation of CuO-CeO2/SiC was created. Copyright (C) 2015, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.

Catalytic Decomposition of Sulfuric Acid over Copper Ferrite in Iodine Sulfur Thermochemical Cycle

Catalytic decomposition of sulfuric acid on composite oxides and Pt/SiC

Study on the High-Performance Catalyst for Sulfuric Acid Decomposition in the IS Cycle

Preparation of Copper Chromite by Vaccum Freezing Drying Method and Its Catalytic Activity for Sulfuric Acid Decomposition

Catalytic Decomposition of Sulfuric Acid over CuO/CeO2 in the Sulfur–iodine Cycle for Hydrogen Production

Catalytic Performance of Semi-Coke on Hydrogen Iodide Decomposition in Sulfur-Iodine Thermochemical Cycle for Carbon Dioxide-Free Hydrogen Production

INET's Catalysts Study for HI Decomposition in the Thermochemical Water-Splitting Iodine–sulfur Process for Hydrogen Production

Sulfuric acid decomposition in the iodine–Sulfur cycle using heat from a very high temperature gas-cooled reactor

Bimetallic catalysts for HI decomposition in the iodine-sulfur thermochemical cycle

Study on Cuo-Ceo2/Sic Catalysts in the Sulfur-Iodine Cycle for Hydrogen Production

SO3 Decomposition over CuO–CeO2 Based Catalysts in the Sulfur–iodine Cycle for Hydrogen Production

Influence of Calcination Temperature on CuO–CeO2/SiC Catalysts for SO3 Decomposition in the Sulfur–iodine Cycle for Hydrogen Production

Researches in the Catalysts for Sulfur Acid Decomposition in Iodine-Sulfur Thermochemical Cycle for Hydrogen Production

THERMODYNAMICS STUDY ON REACTIONS OF SULFUR IODINE THEMOCHEMICAL CYCLE FOR H2S-SPLITTING

Progress of Bunsen reaction study in iodine-sulfur thermochemical cycle

Studies on the Preparation of Active Oxygen-Deficient Copper Ferrite and Its Application for Hydrogen Production Through Thermal Chemical Water Splitting

Purification of Sulfuric and Hydriodic Acids Phases in the Iodine-sulfur Process

The Stability of Pt–Ir/C Bimetallic Catalysts in HI Decomposition of the Iodine–sulfur Hydrogen Production Process

Catalytic decomposition of sulphuric acid in Iodine-Sulphur and Hybrid-Sulphur processes for Hydrogen production: Estimation of effectiveness factor of catalyst

Decomposition of Hydrogen Iodide over Pt–Ir/C Bimetallic Catalyst

Overview of the development of catalysts for HI decomposition in the iodine–sulfur thermochemical cycle at INET