Activated Fly Ash/slag Blended Cement

Feng-Qing Zhao,Wen Ni,Hui-Jun Wang,Hong-Jie Liu

DOI: https://doi.org/10.1016/j.resconrec.2007.04.002

IF: 13.716

2007-01-01

Resources Conservation and Recycling

Abstract:This paper presents the results of the preparation of an ecological cementing material from granulated blast-furnace slag (GBFS) and Class C fly ash (CCFA). The desulphurization gypsum, calcined at 600–800°C for 0.5–1.5h, works as the main ingredient of the activator in the cementing material. The optimized formulation of the cementing material was obtained with the aid of factorial design method: slag, 70%; CCFA, 18%; activator, 12%. The “partial super-fine grinding process” was adopted to improve the performance, i.e., 85% of the mixture is ground to Blaine fineness of 3500cm2/g, 15% further ground to around 5000cm2/g. The compressive strength of 28 days of the cement mortar is up to 49MPa and flexural strength 8.4MPa. The hydration products, investigated by SEM and X-ray diffraction, are mainly ettringite and C–S–H gel.