Electrochemical Properties of Microarc Oxidation Films on a Magnesium Alloy Modified by High-Intensity Pulsed Ion Beam

X. G. Han,X. P. Zhu,M. K. Lei
DOI: https://doi.org/10.1016/j.surfcoat.2011.04.042
2011-01-01
Abstract:Microarc oxidation (MAO) films on AZ31 magnesium alloy were treated by high-intensity pulsed ion beam (HIPIB) irradiation with ion energy of 300keV at ion current density of 200A/cm2. A remelted layer of a few micrometers was produced on irradiated MAO films. The corrosion resistance of MAO films was characterized by potentiodynamic electrochemical test in 3.5% NaCl solution. The anodic polarization behavior of MAO samples exhibited a transition from the active anodic dissolution for the original one to the passivation–pitting breakdown for the modified films. The passivation–pitting breakdown voltage of modified films increased with multi-shot irradiation, i.e. from a value of −1420mV(SCE) at 1 shot to −800mV(SCE) at 5 shots, and the corresponding passivation current density decreased by two orders of magnitude. The irradiated MAO films have a higher corrosion potential than the original one, reaching a maximal value of −1350mV(SCE) at 5 shots from the original −1580mV(SCE). The electrochemical impedance spectrum (EIS) of modified MAO films was measured with varying the immersion time in 3.5% NaCl solution. The Nyquist impedance plots from modified films may show only a capacitive loop at the immersion time of 5h, and the inductive loop occur at longer immersion time, whereas original films presenting both capacitive and inductive loops at all the immersion time. Bode plots of MAO films before and after irradiation were obviously distinguished in shape at low frequency range, especially at short immersion time. The evolution of Nyquist and Bode plots with immersion time was discussed in association with the processes of electrolyte penetration into the MAO structure and resultant reaction at the film-substrate interface. It is concluded that the improvement in the continuity and compaction of MAO films accounts for the enhanced corrosion resistance of the films irradiated by HIPIB.
What problem does this paper attempt to address?