Abstract:We have investigated the effects on the magnetic properties of NiMnSb alloys with the substitution of Cu for Ni. The half-Heusler type alloys, CuxNi1−xMnSb compounds, are fabricated by the arc-melting method and are subsequently annealed at a temperature of 1050K for 24h. It was found that at a temperature of 4K and field of 10kOe for CuxNi1−xMnSb samples, the formula moment remains almost unchanged for x<0.7. With x increasing above 0.7, the formula moment starts to decrease. The Curie temperature and susceptibility for different Cu compositions were measured on SQUID. The paramagnetic Curie temperature is obtained by extrapolation. It shows that the Curie temperature dependence of Cu composition is similar to that of paramagnetic Curie temperature versus Cu composition, which decreases with increasing Cu composition. The relation between Curie temperature and Cu composition can be fitted with the formula, Tc=A–Bx2, which reflects the weakening in exchange energy with substitution of Cu for Ni in NiMnSb alloys. The temperature dependence of susceptibility fitted at high temperature for different Cu compositions shows that with the substitution of Ni by Cu the Curie constant remains almost unchanged which indicates that the total angular momentum and effective moment remain almost unchanged. The laws of temperature dependence of susceptibility are consistent with that of magnetism versus temperature, which originates from the effects of Curie temperature for different Cu compositions. When Cu compositions increases from x=0 to 1, the magnetic properties of the alloys change from ferromagnetism to ferrimagnetism. When x=1 antimagnetism for the sample is exhibited.

Magnetic and electrical properties of the half-Heusler CuxNi1−xMnSb alloys

Magnetic behavior of half-Heusler alloy CuxNi1−xMnSb

The influences on magnetic properties of substitution of Cu for Ni in NiMnSb alloys

Magnetic properties and magnetostriction of ZnxNi 1-xMnSb alloys

Magnetic Properties and Magnetostriction of ZnxNi1-x MnSb Alloys

Magnetic and Magnetocaloric Properties in Cu-doped High Mn Content Mn50Ni40−xCuxSn10 Heusler Alloys

Transport Properties and Magnetoresistance in CoNb1−xMnxSb Half-Heusler Alloys with a Low Temperature Localization

Magnetic Properties and Magnetostriction of Zn<sub>x</sub>Ni<sub>1-x </sub>MnSb Alloys

Development of half metallicity within mixed magnetic phase of Cu$_{1-x}$Co$_x$MnSb alloy

Magnetism and Magnetocaloric Effect in TlCo2−x Ni X S2 (0 $\leqslant$ X $\leqslant$ 0.05)

Magnetism and magnetocaloric effect in TlCo2−x Ni x S2 (0 x 0.05)

Tunable structural and magnetic properties of NiAs-type Mn<i><sub>x</sub></i>Sb (1.00<i>x</i>1.30) compounds

Effects of Substitution of Zn for Ni in NiMnSb Alloys

Structure, Magnetic and Magnetocaloric Properties of Ni2MnGa Heusler Alloy Nanowires

Thermoelectric Performance of Half-Heusler Compounds TiNiSn and TiCoSb

Electron Localization and Spin-Dependent Transport Property of Conb0.6mn0.4sb Half-Heusler Alloy

Probing electronic, magnetic and thermal properties of NiMnSb Half-Heusler alloy for spintronics as an environmentally friendly energy resource: A DFT+U and Monte Carlo study

Tuning effect of Cu doping on martensitic transformation and magnetic and mechanical properties of Heusler alloy Mn50Ni40In10−xCux (x = 0–10) ribbons

Structure, Electrical and Magnetic Properties of Ni<sub>47-x</sub>Mn<sub>42+x</sub>In<sub>11</sub> (x=0, 1, 2) Based Heusler Alloys

Structure and Physical Properties of Quaternary Heusler Alloy NiMnCuSb

Structural and magnetic properties of MnCo1-xFexSi alloys