The influences on magnetic properties of substitution of Cu for Ni in NiMnSb alloys

S.K Ren,W.Q Zou,J Gao,X.L Jiang,F.M Zhang,Y.W Du

DOI: https://doi.org/10.1016/j.ssc.2004.05.007

IF: 1.934

2004-01-01

Solid State Communications

Abstract:We have investigated the effects on magnetic properties of NiMnSb alloys with substitution of Cu for Ni. The half-Heusler type alloys CuxNi1−xMnSb have been fabricated by the arc melting method and subsequently annealed at 1050 K for 24 h. All the samples retain the half-Heusler type structure. Lattice constants increase slightly with increasing Cu composition. It was found that at 300 K and in a field of 10kOe for CuxNi1−xMnSb samples the magnetization almost remains unchanged for x<0.4. With increasing x above 0.4, the magnetization starts to decrease. When x is above 0.8 the magnetization decreases to near zero. At 100 K, the range in which the magnetization does not change expands to x<0.7. A significant magnetization was found with a further increase of x; it approaches zero when x is over 0.9. The Curie temperature decreases with increasing Cu content. The curve of Curie temperature versus Cu composition can be fitted with formula of Tc=A−Bx2, which reflects the weakening in exchange energy with substitution of Cu for Ni in NiMnSb alloys. For x<0.4, little change was found for the magnetostriction. For 0.4<x<0.8, the magnetostriction decreases drastically with increasing Cu composition and decreases near to zero at x=0.8, which is consistent with the dependence of magnetization versus Cu composition.