Abstract:In order to successfully prepare a new advanced TiAlSiN gradient coating with Ti content gradually decreased but Al content gradually increased from the cemented carbide substrate to the outermost coating surface by arc ion plating, we deeply investigated the influence mechanisms of two important process parameters. These parameters include substrate bias voltage and arc current, which affect the mechanical properties and microstructure of the gradient coating. The results show that bias voltage and arc current directly affect the particle accumulation effect on the coating surface and the re-sputtering effect caused by high-energy ion bombardment, thus affecting the deposition efficiency of the coating and the formation of defects such as macro-particles and pits on the coating surface. The increase of bias voltage is conducive to the increase of the density of columnar crystals and nanocrystals. While the increase of arc current makes the coating with high Al content transform from columnar crystals to nanocrystals. The hardness and interfacial adhesion of the gradient coatings showed a tendency of firstly increasing and then decreasing with the increase of both bias voltage and arc current. When the bias voltage and arc current are -80 V and 160 A respectively, the coating has the best mechanical properties, its surface hardness reaches 36.94 GPa, and the interfacial adhesion exceeds 120 N. In addition, with the increase of bias voltage and arc current, particles are deposited on the surface of the coating with higher energy, which leads to the preferential orientation transition from (111) to (200) plane. The high hardness of TiAlSiN coating is mainly due to the formation of high Al content of fcc-TiAlN crystals and amorphous Si3N4 in the gradient-coated surface layer. The results have important theoretical and practical significance for developing new highperformance gradient coating tools.

Study on functionally gradient coatings of Ti–Al–N

PHASE STRUCTURE AND DISTRIBUTION OF Ti-AI-N FUNCTIONAL GRADIENT COATINGS

Properties of TiAlCrN coatings prepared by vacuum cathodic arc ion plating

Effect of Arc Deposition Process on Mechanical Properties and Microstructure of TiAlSiN Gradient Coatings

Effect of CrN Addition on the Structure, Mechanical and Thermal Properties of Ti-Al-N Coating

Tribological Properties and Preparation of (Ti,Al)N Coatings on High Speed Steel Substrate

Functionally Gradient Coating of Aluminum Alloy via In Situ Arc Surface Nitriding with Subsequent Friction Stir Processing

Role of the nitrogen ratio on mechanical properties and wear resistance of CrN/Fe functionally graded coating produced by double glow plasma alloying

Thermal and Thermo-Mechanical Properties of Ti–Al–N and Cr–Al–N Coatings

Microstructure, Oxidation Behavior and Adhesion of a CoNiCrAlTaY Coating Deposited on a High Nb–TiAl Alloy by Plasma Surface Metallizing Technique

Isothermal Oxidation Behaviour of a Gradient NiCoCrAlSiY Coating Deposited by Arc Ion Plating on a Ni-based Single Crystal Superalloy

Effect of nitrogen flow rate on the microstructure, mechanical and tribological properties of CrAlTiN coatings prepared by arc ion plating

Influence of film structure on the microstructure and properties of TiAlN coatings on Al-Si alloys

Structure, mechanical properties and thermal stability of CrAlNbN/TiN multilayers

In-situ Ti(C, N) reinforced AlCoCrFeNiSi-based high entropy alloy coating with functional gradient double-layer structure fabricated by laser cladding

Evaluation of wear resistance of CrN, CrAlN, and TiAlN coatings deposited by multi-arc ion plating on spinning die of Cr12MoV

Microstructure, mechanical and tribological properties of gradient CrAlSiN coatings deposited by magnetron sputtering and arc ion plating technology

Microstructural and Performance Analysis of (TiAl)95−xCu5Nix Coatings Prepared via Laser Surface Cladding on Ti–6Al–4V Substrates

Improvement of Tribological Performance of TiAlNbN Hard Coatings by Adding AlCrN

Effects Of Gradient Multilayer Structure On Tribological Property Of Tialsin Coating

Effect of Gradient Multilayer Design on Tribological Performance of TiN/TiSiN Coatings Prepared by Cathodic Arc Ion Plating