Preparation of Water-Soluble Hyperbranched Poly(sulfone-Amine)s by Polyaddition of N-ethylethylenediamine to Divinyl Sulfone

C Gao,DY Yan,XY Zhu,W Huang

DOI: https://doi.org/10.1016/s0032-3861(01)00256-7

IF: 4.6

2001-01-01

Polymer

Abstract:The new approach for synthesis of hyperbranched polymers from commercially available A2 and BB′2 type monomers has been further developed. Water-soluble hyperbranched poly(sulfone-amine)s with multiple amino end groups were prepared by direct polyaddition of divinyl sulfone (DV, A2) to N-ethylethylenediamine (NDA, BB′2). Effects of reaction conditions such as the feed ratio and solvents on the polymerization have been investigated. When the feed ratio of DV to NDA was equal to 1, no gelation occurred during the polymerization in water or organic solvents. Similarly, when the feed ratio of DV to AP was equal to 3/2, no insoluble or cross-linked material was observed in chloroform or other organic solvents such as N,N-dimethylforamide, N,N-dimethylacetamide and N-methyl-2-pyrrolidone. Interestingly, when water was used as solvent, the reaction mixture got turbid within 15–20min and gelation occurred within 12–15h. The turbid mixture formed during initial stage becomes a transparent solution in aqueous acid, which was coined as ‘pseudo-gelation’. The solubility of the resulting polymer in water is as high as 1.68g/ml. The degree of branching (DB) of all the resulting hyperbranched polymers is higher than 50% and the highest one is 70.9%. The reaction mechanism is presented and demonstrated with FTIR, HPLC and MS. During polymerization, secondary amino groups of NDA react rapidly with vinyl groups of DV within 12s dominantly generating dimers which can be regarded as a new AB′2 type monomer. Further polymerization of the new monomers leads to hyperbranched poly(sulfone-amine)s.