Hyperbranched Polymers Made from A2, B2 and BB′2 Type Monomers, 2. Preparation of Hyperbranched Copoly(sulfone-Amine)s by Polyaddition of N-ethylethylenediamine and Piperazine to Divinylsulfone

C Gao,W Tang,DY Yan,PF Zhu,P Tao

DOI: https://doi.org/10.1016/s0032-3861(00)00757-6

IF: 4.6

2001-01-01

Polymer

Abstract:The new approach for preparation of hyperbranched polymers from commercially available A2 and BB′2 type monomers was further extended to synthesize hyperbranched copolymers. In this work, hyperbranched copoly(sulfone-amine)s were prepared by polyaddition of piperazine (B2) and N-ethylethylenediamine (BB′2) to divinylsulfone (A2). The polymerization mechanism was investigated with FTIR and LC-MSD. During the copolymerization, secondary-amino groups of piperazine and N-ethylethylenediamine react rapidly with vinyl groups of divinylsulfone within 50s, and then the residual vinyl groups react with primary-amino groups resulting in hyperbranched copoly(sulfone-amine)s. The crystallization behaviors of the resulting polymers were characterized with DSC and X-ray diffraction. When the initial mole ratio of B2 to BB′2 is equal to or higher than three, r≥3, resulting copolymers are semi-crystalline, while those with r<3 are amorphous. Interestingly, the resulting polymers with r=3 exhibit the highest melting temperature comparing with other semi-crystalline samples. The degree of branching of hyperbranched copolymers was determined by 1H NMR.