Preparation, Characterization and Electrical Transport Properties of Individual Α-Mno2 and Β-Mno2 Nanorods

Xin-Yu Xue,Li-Li Xing,Yan-Guo Wang,Tai-Hong Wang

DOI: https://doi.org/10.1016/j.solidstatesciences.2009.08.022

IF: 3.752

2009-01-01

Solid State Sciences

Abstract:Electrical transport experiments are performed on individual α-MnO2 and β-MnO2 nanorods. Both of α-MnO2 and β-MnO2 nanorods are synthesized via hydrothermal routes. A three-region method is used to analyze their nonlinear current–voltage characteristics. Under low biases, the effective contact barrier height is roughly estimated to be 0.05eV for α-MnO2 and 0.15eV for β-MnO2, respectively. As the applied bias is high enough, the contact barriers are significantly tilted and the current is largely tunneling. The conductance of α-MnO2 and β-MnO2 nanorods at room temperature is roughly estimated to be 5.98 and 1.74×10−3cm−1Ω−1, respectively. And the thermal-activation energy is roughly estimated to be 0.047 and 0.226eV, respectively. Our results are probably the bases for their applications in nanosized electrical devices.