Preparation and Characterization of Al2O3–TiO2Composite Oxide Nanocrystals
G Xiong,X Wang,LD Lu,XJ Yang,YF Xu
DOI: https://doi.org/10.1006/jssc.1998.7917
IF: 3.3
1998-01-01
Journal of Solid State Chemistry
Abstract:Al2O3–TiO2composite oxide nanocrystals with different Al2O3/TiO2ratios (1/4, 2/3, 3/2, and 4/1) were prepared by the poly(ethylene glycol) (PEG) sol–gel method. The preparation process was monitored by thermogravimetric analysis and differential scanning calorimetry (TGA–DSC). Nanocrystal particles of these composite oxides obtained at various heat-treating temperatures (400–1100°C) were characterized in terms of morphology, size, specific surface area, composition, and structure by transmission electron microscopy (TEM), BET specific surface area analysis, and X-ray powder diffractometry (XRD). Nanoparticles of Al2O3–TiO2with grain sizes in the range 1–150 nm and specific surface areas of 4.3–136 m2/g could be obtained under different conditions. The morphology of the particles changed from spherical to cubic with increasing heat-treatment temperature. Anatase was stabilized in these composite nanomaterials and the mechanism was discussed. The change of the particles specific surface areas with increase of the Al2O3/TiO2ratio was researched. The Al2O3–TiO2composite oxide nanocrystals could catalyze the polymerization of maleic anhydride and may provide a route to obtain a product without rings at the end groups.