Study of styrene-butadiene rubber/halloysite nanotubes nanocomposites modified by methacrylic acid

LEI Yan-da,ZOU Quan-liang,DU Ming-liang,GUO Bao-chun,JIA De-min

DOI: https://doi.org/10.3969/j.issn.1673-9981.2008.04.011

2008-01-01

Abstract:A new kind of rubber reinforcing agent from non-petroleum resource,halloysite nanotubes(HNTs) were adopted to reinforce styrene-butadiene rubber(SBR) in this paper.Methacrylic acid(MAC) was employed as interfacial modifier to improve the comprehensive properties of the vulcanizates.The effects of MAC loading on vulcanization characteristics of SBR/HNTs compounds,mechanical properties of vulcanizates and crosslink density(based on Flory-Rehner equation) were investigated.The results showed that HNTs could increase the tensile strength and modulus of SBR vulcanizates.The scorch time of the compounds was basically independent of the MAC content although the torsion of the compounds before scorch was decreased with MAC content.SBR/HNTs compounds incorporated with MAC showed greatly increased tensile strength and modulus.When the MAC loading was higher than 5 phr,translucent samples were surprisingly obtained,indicating uniform dispersion of halloysite nanotubes in the rubber matrix.When the contents of HNTs and MAC were 40 phr and 12 phr respectively,300% stress,tensile strength and tear strength of the vulcanite reached 6.3 MPa,15.1 MPa and 51.3 kN/m respectively,with elongation at break up to 700%.The crosslink densities calculated from Flory-Rehner equation indicated that the total crosslink density and the ionic crosslink density of the vulcanizates were increased while the effect on the ionic crosslink density was more obvious.