Abstract:A novel pathway for the magnesiothermic reduction of boron oxide and magnesium dodecaboride (MgB12) in the presence of carbon by a self-propagating high-temperature synthesis method was proposed that was aimed at the direct preparation of boron carbide nanopowder. The combined utilization of two boron sources, boron oxide and MgB12, allowed tailoring the overall caloric effect of the process, increasing the yield of the target product and lessening the laborious leaching process. In addition, it is an alternative way to utilize magnesium borides, which are inevitable side products at boron production. Multivariate thermodynamic calculations performed in the B2O3-MgB12-Mg-C system allowed estimating equilibrium compositions of the products and deducing the optimum composition of the initial mixture for obtaining B4C. For the latter, the adiabatic temperature (Tad) is 2100 °C, which is theoretically enough for the implementation of the self-propagating reaction. The combustion reaction was shown to be extremely sensitive to the initial mixture composition, external pressure, as well as sample diameter (heat losses). It proceeds in self-oscillatory mode and leads to the product of a layered macrostructure. The combustion product was then consolidated by the spark plasma sintering technique at different conditions. Vickers microhardness was measured, and the wear erosion behavior was examined. The variation in lattice parameters of boron carbide reflected the influence of synthesis, sintering and erosion conditions on the ordering/disordering of the boron carbide structure.

Synthesis and Characterization of Boron Carbide Nanobelts

Formation of borate zinc (ZnB4O7) nanotubes

Synthesis of Boron and Boride Compounds Nanowire Arrays by Chemical Vapor Deposition

Synthesis of vertically aligned boron nitride nanotubes with a template of single-walled carbon nanotubes

Crystalline boron oxide nanowires on silicon substrate

Preparation and Structure of Boron Carbide Nanowires

Synthesis of boron carbide nanoflakes via a bamboo-based carbon thermal reduction method

Aligned single crystal Al-catalyzed boron nanorods on Si substrates

Morphology and diameter controllable synthesis of boron nanowires

Boron carbide nanowires with uniform CNx coatings

Synthesis of Aluminium Borate Nanowires by Sol–gel Method

Straight boron carbide nanorods prepared from carbon nanotubes

High-quality boron carbide nanowires prepared by catalyst-free template growth method

Facile Synthesis and Characterization of Hexagonal Boron Nitride Nanoplates by Two‐Step Route

Novel Pathway for the Combustion Synthesis and Consolidation of Boron Carbide

Short belt-like Ca2B2O5·H2O nanostructures: Hydrothermal formation, FT-IR, thermal decomposition, and optical properties

Synthesis of Boron Carbide Powder Through Gas-Solid Reaction Method Using Nanoporous Carbon As Carbon Source

Effective Growth of Boron Nitride Nanotubes

The Hydrothermal Method of Preparing Boron–Saccharide Precursors for the Synthesis of Boron Carbide and Its Influence on the Morphology and Phase Composition of the Obtained Products

Growth of Boron Nitride Nanotubes from Magnesium-Based Catalysts

Growth of boron nitride nanotubes from magnesium diboride catalysts