Abstract:CdxZn1−xS nanoparticles have been successfully synthesized by SILAR method on the base of functionalized nitrile butadiene rubber (FNBR). Because the solubility product of CdS (Ksp=8.0×10−27) is lesser than that of ZnS (Ksp=1.6×10−12), the nucleation rate of ZnS was high at the start of the reaction, but the particle growth rate and stability of CdS is high in the further course of the reaction. CdxZn1−xS nanoparticles have been synthesized on the base of functionalized nitrile butadiene rubber (FNBR) by SILAR method and characterized by various techniques. Both binary and ternary sulfide nanocrystals have been obtained in the cubic phase with very high purity at room temperature. The average particle size decreased from 2.49 nm to 2.22 nm and then increased to 2.44 nm by the increasing of zinc concentration from 25 % to 50 % and 75 %. The calculated Young's modulus for (111), (220) and (311) planes are 97.84, 78.51 and 64.33 m2 N−1 for CdS and 95.84, 69.68, 53.42 m2 N−1 for ZnS, respectively. The band corresponding PO32− (977 cm−1) shifted to 969, 975, 972, 973, and 972 cm−1 upon the formation of CdS, ZnS, Cd0.5Zn0.5S, Cd0.75Zn0.25S and Cd0.25Zn0.75S nanoparticles into FNBR matrix, which is explained by Hooke's Law. EPR spectra of CdS/FNBR nanocomposite show broad and singlet asymmetric, isotropic symmetry (gx=gy=gz). The appearance of a new line in the 3518 G magnetic field is observed in both CdS and Cd0.5Zn0.5S compounds' spectra.The total mass loss of the samples NBR, FNBR, Cd2+ and Zn2+ ions containing FNBR are 93.76, 59.77, 60.03 and 57.79 %, respectively. High crystallinity is caused by complete interaction of metal ions with functional groups during the nucleation.

Synthesis and characterization of CdS/BSA nanocomposites

Synthesis of Mesoporous CdS/titania Composites with Visible Light Photocatalytic Activities

Novel C3N4–CdS Composite Photocatalysts with Organic–inorganic Heterojunctions: in Situ Synthesis, Exceptional Activity, High Stability and Photocatalytic Mechanism

Synthesis and Characterization of Polymer-Cds Nanocomposites

Synthesis of CdS nanoparticles in water/DMF medium: an investigation on the effect of time and microwave irradiation

Synthesis and characterization of multiwalled carbon nanotube/CdS core/shell heterostructures

Synthesis and Luminescence Properties of Cds Nanoparticles

THE OPTICAL AND ELECTRICAL PROPERTIES OF SPAn/CdS NANOCOMPOSITES PREPARED BY SOLVOTHERMAL METHOD

Noninjection Synthesis of CdS and Alloyed CdS x Se 1−x Nanocrystals Without Nucleation Initiators

Synthesis and visible-light photocatalytic properties of BiOBr/CdS nanomaterials

The Effect of the Ratio of Thiourea to Cd2+ on the Properties of CdS Nanoparticles

Synthesis of nano-CdxZn1-xS by precipitate-hydrothermal method and its photocatalytic activities

Synthesis, structural and optical characterization of CdxZn1−xS/FNBRnanocomposites

Preparation of ZnxCd1-xS Nanocomposites in Polymer Matrices and Their Photophysical Properties

Aqueous synthesis and characterization of bovine hemoglobin-conjugated cadmium sulfide nanocrystals

Facile Synthesis and Antibacterial Applications of Cuprous Oxide/bovine Serum Albumin Hierarchical Nanocomposite Particles

Controllable Synthesis of Functionalized CdS Nanocrystals and CdS/PMMA Nanocomposite Hybrids

Synthesis Of Lead Sulfide/(Polyvinyl Acetate) Nanocomposites With Controllable Morphology

Facile Synthesis and Luminescence Characteristics of High-Quality Cds: Eu/Zns Core/Shell Nanocrystals with Biocompatibility

Effect of CdS Distribution on the Photocatalytic Performance of Resin-Cds Nanocomposites

Synthesis and Optical Properties of Nanosized CdS Prepared in a Quaternary CTAB/n-hexanol/n-heptane/water Reverse Micelle