Process of rare earth conversion coating on the surface of graphite fiber reinforcement aluminum matrix composites

WANG Chunyu,ZHANG Qiang,KANG Pengchao,JIANG Longtao,WU Gaohui

DOI: https://doi.org/10.3321/j.issn:1001-053x.2008.06.011

2008-01-01

Abstract:A Ce conversion coating,which is non-toxic and non-pollution,was prepared by chemical dipping immersion treatment on graphite fibers reinforce aluminum(Gr/Al) composite surface.It is shown that the graphite fiber and aluminum alloy surfaces both are coated by the Ce conversion coating,and the microstructure of the coating is dried-mud-like.Energy dispersive spectroscopy(EDS) indicates that the major elements distributing on the coating are Al,O,C,Si,Ce,and Mg, and the mass fraction of Ce is 14.44wt% after coating for 30 min but increases to 47.48wt% after coating for 120 min.The formation mechanism of coating micro-cracks was put forward.The micro-cathodic formation mechanism can explain the characters of the coatings.The Ce conversion coating becomes a barrier of O2 diffusion and electron transmitting,and oxygen absorption and hydrogen separation were both inhibited.