Abstract:The C=C double bonds in the main chain of hydroxyl-terminated polybutadiene (DHTPB), obtained by the degradation of polybutadiene rubber, were partially epoxided using m-chloroperoxybenzoic acid (mCPBA) as epoxidation reagent. A series of epoxided HTPBs (EHTPB) with different epoxy contents (5%, 10% and 15%) were prepared by tuning the molar ratio of mCPBA to C=C double bonds. The structures of EHTPBs were characterized by Fourier transform-infrared (FTIR), nuclear magnetic resonance (H-1-NMR) spectroscopy and gel permeation chromatography (GPC). The epoxy percent in EHTPBs from H-1-NMR spectra was in accordance with the design. In addition, a series of EHTPB-based polyurethane elastomers (EPU) were prepared by the reaction between EHTPB and 4,4'-diphenylmethane diisocyanate with 1,4-butanediol as a chain extender. Mechanical and thermal properties of the EPU samples were characterized by tensile test, differential scanning calorimetry (DSC) and thermal gravity analysis (TGA). With increased epoxy percent in EHTPB, the Young's modulus and the tensile strength of the EPU samples increased, whereas the elongation at break decreased. The sample EPU10 prepared with 10% of epoxy had the best mechanical properties with 8.82 MPa as Young's modulus, 7.83 MPa as tensile strength, and (485 +/- 23)% as elongation at break. The elasticity recovery of the EPU sample was slightly better than HTPB-based PU (EPU0). The results with TGA test showed that the thermal degradation of EPU, similar to EPU0, was divided into three stages. However, the EPU samples had better thermal stability with the initial degradation temperature at 210 degrees C, about 30 degrees C higher than that of EPU0. The DSC results showed that the glass transition temperature (T-g) of EPU gradually increased as epoxy percent was increased, though still lower than that of HTPB (FHTPB) based PUs prepared by free-radical polymerization.

Preparation, Morphology, and Properties of Polyurethane–urea Elastomers Derived from Sulphone‐containing Aromatic Diamine

Preparation and Properties of Epoxided Hydroxyl-terminated Polybutadiene Based Polyurethane Elastomers

Microphase Separation and Properties of Polyurethane Elastomers Containing Sulfuryl Group Chain-Extender

Synthesis and properties of elastomeric polyurethane for grouting

Synthesis and Characterization of Polyurethane Urea Based on Fluorine‐containing Bisphenoxydiamine

Mechanical and surface properties of polysulfide-based polyurea modified with aminoethylaminopropyl poly(dimethylsiloxane)

Synthesis and Properties of Polyurethane Modified with Aminoethylaminopropyl Poly(dimethyl Siloxane)

Synthesis and Properties Characterization of Thermoplastic Sulfone-Polyetheramide Elastomers

The Structural and Mechanical Properties of Polysulfide‐based Polyurea

Synthesis and Properties of Polybutadiene-Containing Polyurethane-ureas Modified with Aminoethylaminopropyl Poly(dimethyl Siloxane)

Preparation of Polyurethane‐Urea Elastomers Using Low Molecular Weight Aliphatic Diamines Enabled by Reversible CO2 Chemistry

Synthesis,characterization and properties of novel sulfonated poly(arylene ether sulfones)

Influence of Amine Chain Extenders on Morphology and Performances of Poly(dimethylsiloxane) Based Poly(urea‐urethane) Elastomers

Synthesis and Characterization of Sulfonated Polyamides

Structure and properties of polyurea elastomers based on aromatic amine-terminated polytetramethylene ether

Structure-property behavior of polyurea synthesized with different kinds of amino polyether

Synthesis and Characterization of Poly(imide‐urethane) Based on Novel Chain‐extender Containing Both Imide and Sulphone Functions

Preparation and characterization of polyurethan-block-poly(trifluoropropylmethyl)siloxane elastomers

Synthesis and Characterization of Linear Polyisoprene Supramolecular Elastomers Based on Quadruple Hydrogen Bonding

Preparation and characterization of polyurethan-<i>block</i>-poly(trifluoro- propylmethyl)siloxane elastomers

Synthesis of N-phenylaminomethyl POSS and its utilization in polyurethane