Half-titanocenes Catalysts Based on Titamium-phosphinimide for Producing Atactic Elastomeric Polypropylenes with High Molecular Weight
Jian-jun Chen,Tie-shi Wang,Zheng-wei Tang,Yi-bing Xu,Lin Xu,Mao-sheng Cao,Zeng-guo Feng
DOI: https://doi.org/10.11777/j.issn1000-3304.2017.16331
2017-01-01
Acta Polymerica Sinica
Abstract:Two half-titanocenes, containing a phosphinimide ligand [(t- Bu)(3)P=N] CpTiCl2 (PT1) and [(t- Bu)(3)P=N] CpTiMe2 (PT2) as the main catalysts for olefin polymerization, were examined in propylene polymerization in the presence of methylaluminoxane (MAO) or [Ph3C][B(C6F5)(4)] as the co-catalyst. The catalytic performance was also compared with typical {rac-[En(IndH(4))(2)] ZrC12} (1), CpTiCl3 (2) and Cp2TiCl2 (3) catalysts. The effects of experimental conditions, including feeding molar ratio of the co-catalyst to the main catalyst [Al]/[Ti], temperature, propylene pressure and reaction time, on the catalytic activity of the polymerization, the molecular weight and molecular weight distribution of the resulting polypropylenes (PPs) were investigated in detail. A maximal activity of 3.25 x 10(6) g PP/ molTi . h was attained using PT2/[Ph3C][B(C6F5)(4)] in the presence of MAO at [Al]/[Ti] =800. Meanwhile, a highest molecular weight of M-w =4.42 x 10(5) with a molecular weight distribution of 1.73 was reached with PT1/ MAO at [Al]/[Ti]=1200. The molecular weights were increased with decreased polymerization temperature, increased reaction pressure and polymerization time (t(p)). Interestingly, it was noted that an asymptotic plot of M-w versus t(p) was almost linear up to 15 min, indicating a "single-site" catalytic polymerization. C-13-NMR and IR analyses revealed that the resulting polymers were atactic PPs, which were more or less syndiotactically enriched atactic ones with higher diads r (62.28%) than m (37.72%). Furthermore, a calculated value of 1.04 for [mr/(2mm + mr)] + [mr/(2rr + mr)] indicated that the polymerization was conducted in agreement with the statistical model of Bernoullian. DSC measurements further confirmed the atactic microstructure of the PPs with a glass transition temperature (T-g) ranged from -3.7 degrees C to -2.6 degrees C without any melting endotherm. Accordingly, the PPs produced in this study by the phosphinimide catalysts were mainly made up of 1,2-insertion units together with a small number of 2,1-insertion units.