Abstract:In this study, NiCrSiB-SiC composite coatings were prepared on 16Mn low-carbon steel by vacuum cladding technology using SiC and NiCrSiB mixed powders as raw materials for enhancing their wear resistance. The effects of different content of SiC particles on the microstructure evolution, mechanical and abrasive wear properties of the coatings were investigated. The results showed that SiC particles in all the NiCrSiB-SiC composite coatings with different SiC contents were completely decomposed into C and Si under the catalysis of Ni-based alloy. The out-diffused Si into the coating mainly led to the formation of the Ni 3 Si eutectic phase, while the out-diffused C introduced M 7 C 3 , M 3 C 2 , M 2 (C, B) and other hard phases. Besides, C also diffused to the substrate, leading to a carburizing effect, which remarkably enhanced the mechanical properties of the substrate. In the NiCrSiB-SiC composite coatings with high SiC content, the decomposition of SiC led to the remaining graphite phase. However, once the concentration of SiC was over high, excess graphite would deteriorate the compactness and adhesion of the coating, weakening its wear performance. The nanoindentation and abrasive wear experiments revealed that the composite coating with 5 wt% SiC particles had lower elastic modulus ( E ), higher hardness ( H ), H / E , and H 3 / E 2 , and its wear volume was only 1/10 of that of the substrate, indicating the best mechanical and wear properties. The excellent wear performance can be attributed to the combination of the in-situ formed carbides and borides hard reinforcing phases and the tough coating matrix composed of Fe and Si dissolved γ-Ni and Ni 3 Si eutectic phase.

Structure and performance of brush-electroplated nickel-based nano SiC-Al2O3 composite coating

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Preparation, Microstructure and Tribological Properties of Nano-Al2o3/Ni Brush Plated Composite Coatings

Wear resistance of Ni/nano-Al2O3 composite coatings by brush electroplating

Characterization and Wear Behaviors of Electrodeposited Ni-MoS2/SiC Composite Coating

Electrochemical Properties and XPS Analysis of Ni-B/SiC Nanocomposite Coatings

Comparative study on the wear resistance and corrosion resistance of NiW and NiCoW composite coatings with micro- and nano-SiC particles

Electrochemical deposition and tribological behaviour of Ni and Ni–Co metal matrix composites with SiC nano-particles

Enhanced Mechanical and Tribological Capabilities of a Silicon Aluminum Alloy with an Electroplated Ni–Co–P/Si3N4 Composite Coating

Wear Property of Nickel Matrix Nano-Al2O3 Electro-plating Composite Coating in Lubricated Condition Containing Solid Particles

A Comprehensive Study on the Characteristics of Electro-brush Nickel Matrix Composite Coats

Effect of SiC Contents on Wear Resistance Performance of Electro-Codeposited Ni-SiC Composite Coatings

Preparation, Mechanical Properties and Wear Resistance of Ni–W/SiC Nanocomposite Coatings

Enhanced mechanical and wear properties of Ni-W-SiC composite coatings by synergistic influence of micro-nano SiC mixture

Study of fabrication and wear properties of Ni–SiC composite coatings on A356 aluminum alloy

Microstructure evolution, mechanical and abrasive wear properties of NiCrSiB-SiC composite coatings prepared on 16Mn low-carbon steel by Ni-based alloy catalyzed SiC decomposition

Technology and Performance of Brush Plating Al/Cu Composite Coatings

High Temperature Tribology Behaviors of Brush Plated Ni–W–Co/SiC Composite Coating

Investigation on Microstructure and Properties of the Electrodeposited Ni-SiC Composite Coating

Electroless Ni-P-Sic Composite Coatings with Superfine Particles

Effect of SiC Nanoparticles on the Structure and Properties of Ni+W-SiC Nanocoatings