Study on f-CaO digestion mechanism of high alkalinity slags with iron ore tailings

Zhang Yuzhu,Xing Hongwei,Lei Yunbo,Long Yue,Hu Changqing,Tian Tielei

2012-01-01

Abstract:The high alkalinity steel slag modified by Tang Shan iron ore tailings at high temperature eliminated the f-CaO content efficiently.The digestion effects of iron ore tailings(3%,5% and 9%),reaction temperatures(1 500℃,1 550℃ and 1 580℃) and holding times(10 min,20 min and 30 min) on eliminating the f-CaO in high alkalinity slag were investigated by orthogonal test.The results show that iron ore tailings can eliminate the f-CaO content effectively of high alkalinity steel slag,the average content of f-CaO in modified slag was 1.17% and the eliminate rate was 76.27%.Moreover,the content of iron ore tailings had a greater impact on f-CaO digestion and the range value for 0.41%.The temperature was less and range value for 0.32%.The minimal impact was holding time and range value for 0.06%.Eventually,according to X-ray diffraction analysis,the mineral composition of modified slag was mainly magnetite phase and calcium and magnesium olivine phase,C2S phase,C3S phase,magnesium iron spinal phase and iron calcium phase,iron aluminum calcium phase.