Abstract:The 2195 Al-Cu-Li alloy is widely utilized in the aerospace industry due to its lightweight nature and high strength. Consequently, gaining a comprehensive understanding of techniques to enhance its microstructural and mechanical properties is crucial for the consistent production of reliable and high-strength aerospace components. In this investigation, a pristine 2195 industrial ingot was subject to three distinct forging pretreatments: PT1, which involved a direct three upsetting and three stretching (3U3S) process; PT2, which combined double stage homogenization (DH) with 3U3S; and PT3, which involved DH along with six upsetting and six stretching (6U6S). Subsequent warm deformation and T8 aging treatment were applied to the pretreated forgings. The microstructure evolution during the processes and the final mechanical properties in three orthogonal dimensions were examined. The findings revealed that the combination of DH and multi-dimensional forging (MDF) facilitated the dissolution of non-equilibrium phases to a greater extent. Consequently, the main strengthening phase transformed from the T 1 + δ` phase observed in PT1 to the denser T1 + little θ` phase observed in PT2 and PT3 after T8 aging treatment. Notably, the tensile strength and yield strength of PT2 and PT3 specimens increased by 20-30 MPa in all three directions. Moreover, the MDF process accelerated the recrystallization behavior from PT1 to PT3, resulting in a gradual reduction in the average grain size of the pretreated samples from 356 μm to 186 μm. Following warm forging and T8 aging, the grains exhibited a finer and equiaxed structure. Additionally, the coarse phase was identified as the primary source of transgranular cracking. The coarse phases within the matrix became more homogeneous and finer from PT1 to PT3, with a gradual decrease in their area fraction. On the fracture surfaces, the aggregation of coarse phases diminished. Consequently, the elongation in the z-direction improved, and the elongation anisotropy and standard deviation decreased in all three directions for PT3 specimens. The findings presented in this study provide valuable insights into the high-performance manufacturing of Al-Cu-Li alloys.

Defect Analysis of Complex-Shape Aluminum Alloy Forging

Study on Simulation of Stamping Forming and Die Surface Optimization of Aluminum Alloy Plate

Finite Element Simulation and Analysis of Deformation in Machining of Aeronautical Aluminum Alloy Thin-Walled Workpiece

Failure control on hydroforming process of thin-walled aluminum alloy with complex surface covers

Deformation Characteristics and Microstructure Analysis of Aluminum Alloy Component with Complex Shape by Cold Orbital Forming

Advances on the Deformation Mechanism and Forgingtechnology of 300M High-Strength Steel Heavy Componentsin the Whole Forging Process

Analysis on Formation Causes for Defects of Powder Metallurgy Flyweights

Forming of Inner Faults Originating from Inclusions in the Heavy Forgings and the Process of Forging Control

Investigation of forming defects in 5A06 aluminum alloy cold stamping of thin-walled shell with corner

Effect of Forging on Microstructure and Properties of Al-9Si-5Cu-0.2Zr-0.1Sr-0.16Ti-0.1Ce Cast Aluminum Alloy

Possibilities of Measuring and Detecting Defects of Forged Parts in Die Hot-Forging Processes

Effect of forging pretreatment on the microstructures and mechanical properties of the Al-Cu-Li alloy

Microstructure Refinement and Crack Initiation in the Forging Process

Investigation of the Penetration Performance of the Radial Forging Process for Wrought Aluminium Alloy

An innovative thermal simulation study of microstructure improvement by delay forging during solidification

Effect of Cold Pressing Deformation on Microstructure and Residual Stress of 7050 Aluminum Alloy Die Forgings

Study on Hot Deformation Behavior and Bending Forging Process of 7075 Aluminum Alloy

The Mechanism of Faults Originating from Inclusions in the Plastic Deformation Processes of Heavy Forging

Microstructural evolutions and mechanical properties of 6082 aluminum alloy part produced by a solution-forging integrated process

Optimization of multi-directional forging parameters of large-scale Mg-Gd-Y-Zn-Zr alloy forged part guided by finite element simulation

Friction Characteristics Analysis of Symmetric Aluminum Alloy Parts in Warm Forming Process