Evaluation and mechanism of a new dental machinable zirconium oxlde/La-monazite diphase ceramic
Shen Wang,Bao-wei Zhang,feng Gu
DOI: https://doi.org/10.3969/j.issn.1673-8225.2009.29.018
2009-01-01
Abstract:BACKGROUND: Previous research has reported that a certain content of assistant phase, such as phosphoric acid/rare earth compound, with low mechanical strength, which was added in zirconium oxide, could decrease the strength and reduce processing cost OBJECTIVE: To evaluate mechanical and processing performances of oral machinable zirconium oxide/La-monazite diphase (LaPO 4/3Y-ZrO 2) ceramic. DESIGN, TIME AND SETTING: A contrast observation was performed at Shanghai Institute of Oral Medicine, Advanced Laboratory of Inorganic Materials Processing, Materials College of Shanghai University from July 2005 to June 2008. MATERIALS: 3Y-ZrO 2, LaPO 4, and Y 2O 3 powder was used to make LaPO 4/3Y-ZrO 2 ceramic, which was divided into 0%, 10%, 20%, 30%, and 40% groups. METHODS: Bending strength at three points were detected using EZ-100 omnipotent apparatus, fracture toughness was measured with indentation method, and Vickers hardness was tested using microhardness apparatus. The samples were tested on CAD/CAM system. The preset time of cutting was 320 seconds, of which whether the LaPO 4/3Y-ZrO 2 ceramic could finish the inlay processing or not. The samples were fixed on desk-top driller, and the drilling depth was tested using carbide drill at constant velocity and axonal pressure. Morphology of bending incision was observed under scanning electron microscope. MAIN OUTCOME MEASURES: Bending strength at three points, fracture toughness, Vickers hardness, cutability, drilling depth, and morphology of bending incision. RESULTS: Circled digit one With the increasing content of LaPO 4, bending strength and Vickers hardness were decreased; fracture toughness in the 10% LaPO 4 group was higher than 0% LaPO 4 group; finally, the fracture toughness decreased from 6.62 MPa·m 1/2 to 2.10 MPa·min. Circled digit two Cutting test demonstrated that 30% and 40% LaPO 4 could finish the inlay processing within the predetermined time; however, 0%, 10%, and 20% LaPO 4 did not finish the inlay processing. Circled digit three Drilling test indicated that with the increasing content of LaPO 4, drilling depth of LaPO 4/3Y-ZrO 2 ceramic was gradually increased. Circled digit four Removal of crystal grain was the major breakage style of LaPO 4/3Y-ZrO 2 ceramic, while LaPO 4 showed a multi-layered shape. CONCLUSION: New ZrO 2/LaPO 4 machinable ceramic with different mechanical strengths could be obtained by changing LaPO 4 content which makes sure the processing performance and references the toughness. LaPO 4/3Y-ZrO 2 ceramic with different ratios benefits for different clinical repairing conditions.