Effect of AN Content on Vulcanization Reaction of NBR Compounds

Li Liu,Baogang Zhang,Huai Yang

2012-01-01

Abstract:Effect of acrylonitrile(AN) content and carbon black on nitrile butadiene rubber(NBR)vulcanization reaction was studied by DSC in this paper.The results show that as AN content increases from 18.8% to 43.3%,the physical cross-linking increases by 20% and the chemical cross-linking is increased by 73%.The vulcanization of NBR compounds contains two stages: sulfur vulcanization and double bond crosslinking.When AN content increases,curing reaction temperature compound reduces,and heat release rate reduces at the first stage,while it increases at the second stage.After the addition of carbon black,the curing reaction is improved,chemical cross-linking density is increased and heat release of vulcanization reduces.With acrylonitrile content increasing,the initial curing temperature increases by 34 ℃ without carbon black,but only by 12 ℃ with carbon black.In addition,the content of acrylonitrile is lower,the influence of carbon black on curing reaction is larger.