Abstract:Polyethersulfone (PES) hollow fiber ultrafiltration (UF) membranes were fabricated by the dry/wet-spinning method; hydrophobic PDMS/PES composite membranes which were supported by self-prepared PES hollow fiber UF membranes were prepared for the pervaporation (PV) separation of ethanol from water. Impacts of PES support layer on the PV performances of PDMS/PES composite membranes were studied. Experimental results showed that, while working as a support to PDMS active layer, PES hollow fiber membrane could affect the PV performance of PDMS/PES membranes greatly. Pervaporation performance of the membrane which its PES support layer had bigger porosity and bigger mean pore size was apparently superior to that of the membrane which its PES support layer had smaller porosity and smaller mean pore size. After being treated with ethanol and hexane, PES membrane was dried in air for 20min before being immersed in PDMS coating solution; the prepared PDMS/PES membrane had the best PV performance with a permeate flux of 330g/(m(2)h) and a separation factor of 5.8. Effects of process parameters, such as feed temperature, permeate pressure, and feed flow rate, on membrane properties were investigated. For the separation of a 5wt.% ethanol-water mixture, with an increase in feed temperature from 30 to 60 degrees C, water flux and ethanol flux increased from 51 to 328g/(m(2)h) and from 14 to 88g/(m(2)h), respectively; the variation of permeation flux followed the Arrhenius relationship and the activation energy values for water and ethanol were 54.54 and 53.44 kJ/mol, respectively; separation factor varied from 5.1 to 6.0. When the feed temperature was 50 degrees C and feed concentration was 5wt.%, with an increase in permeate-side pressure from 1 to 40mmHg, water flux dropped sharply from 334 to 14g/(m(2)h) and ethanol flux dropped moderately from 82 to 22g/(m(2)h), and as a result, separation factor increased. With the increase in feed flow rate from 0.1 to 10L/min, both flux and separation factor increased rapidly at first and then leveled off at 2L/min for the reason of concentration polarization.

Preparation and pervaporation performance of surface crosslinked PVA/PES composite membrane

Enhancing Structural Stability and Pervaporation Performance of Composite Membranes by Coating Gelatin Onto Hydrophilically Modified Support Layer

Integral Pva-Pes Composite Membranes by Surface Segregation Method for Pervaporation Dehydration of Ethanol

Modification of poly(vinylidene fluoride)/polyethersulfone blend membrane with polyvinyl alcohol for improving antifouling ability

Pervaporation Separation of Ethanol from Aqueous Solution by PDMS Membranes Crosslinked with VTES

Pervaporation dehydration of ethyl acetate aqueous solution using the doubly modified polyvinyl alcohol (PVA) composite membrane

Effects of PES support layer structure on pervaporation performances of PDMS/PES hollow fiber composite membranes

Designing High-Performance Pervaporation Membranes with Hierarchical Hydrophobic-Hydrophilic Coating Layers

Preparation of PVA-TEOS/PAN composite membrane and its application in pervaporation separation of ethyl acetate-water solution

Enhancing the Separation Performance by Introducing Bioadhesive Bonding Layer in Composite Pervaporation Membranes for Ethanol Dehydration

Poly(Vinyl Alcohol)/Polyvinylpyrrolidone Blending Membranes:Preparation,Characterization and Dehydration of Ethyl Acetate/Ethanol/Water Azeotrope by Pervaporation

Preparation and pervaporation performance of PVA membrane with biomimetic modified silica nanoparticles as coating

Pervaporation Separation of Ethylene Glycol/water Mixtures Through Surface Crosslinked PVA Membranes: Coupling Effect and Separation Performance Analysis

Preparation of PDMS/PES hollow fiber composite pervaporation membrane

PVA–GPTMS/TEOS Hybrid Pervaporation Membrane for Dehydration of Ethylene Glycol Aqueous Solution

Novel PVA–silica Nanocomposite Membrane for Pervaporative Dehydration of Ethylene Glycol Aqueous Solution

Preparation and characterization of cross-linked poly (vinyl alcohol)/hyperbranched polyester membrane for the pervaporation dehydration of ethylene glycol solution

High performance composite membranes with a polycarbophil calcium transition layer for pervaporation dehydration of ethanol

Enhancing the Antifouling Property of Polyethersulfone Ultrafiltration Membranes Through Surface Adsorption-Crosslinking of Poly(Vinyl Alcohol)

Polyvinyl Alcohol/polysulfone (PVA/PSF) Hollow Fiber Composite Membranes for Pervaporation Separation of Ethanol/water Solution

Research of a PVA Composite Ultrafiltration Membrane Used in Oil-in-water