Abstract:Thermal decomposition was the prerequisite and basis for the utilization of magnesite resources. However, the calcination of magnesite was usually accompanied by high energy consumption, which not only caused serious waste of magnesite resources, but also restricted its high value-added utilization. Therefore, calcination conditions were the key to controlling thermal decomposition process of magnesite. The kinetics of high-grade magnesite thermal decomposition was elaborated by non-isothermal thermogravimetric analysis, and meanwhile the effect of heating rate on the magnesite thermal decomposition reaction and morphology of MgO particles were characterized. Both Doyle and Gorbatchev approximate functions were used to simulate the magnesite thermal decomposition process, where the experimental data (correlation coefficient) fitted by the latter could obtain more acceptable kinetic parameters of the magnesite thermal decomposition. The good linear relationship between the activation energy and the pre-finger factor allowed for a kinetic compensation of the thermal decomposition of magnesite. Furthermore, higher heating rate induced the formation of terraced grains, grain network group, cubic grains, and spherical grains for the samples sintered at 1200 degrees C. The heating rate largely affected the magnesite particle morphology, grain size distribution and activity, and also provided important technical indicators in the actual production of magnesia refractory raw materials.

Study on the Preparation and Thermal Decomposition Dynamics of Magnesium Hydroxide Nanorods

The Non-isothermal Kinetic Analysis of Thermal Decomposition of Mg(OH)2

A study on multistep thermal decomposition behavior and kinetics of magnesium nitrate hydrate

Non-isothermal Decomposition Kinetics of Nano-Mg(oh)2 Using Thermal Gravimetric Analysis

MgO nanostructures synthesized by thermal evaporation

Synthesis of Magnesium Borate Nanorods by Sol-Gel Process

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

Preparation of Magnesia Nanoballs from Dolomite

Formation of rod-like Mg(OH)2 nanocrystallites under hydrothermal conditions and the conversion to MgO nanorods by thermal dehydration

Preparation of Mg(Oh)(2) Nanorods

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

Preparation and thermal decomposition of 5Mg(OH)2·MgSO4·2H2O nanowhiskers

Nanoscale magnesium hydroxide and magnesium oxide powders: Control over size, shape, and structure via hydrothermal synthesis

Preparation of Nano-magnesia by Homogeneous Precipitation

Preparation of MnO_2 Nanorod and Its Catalytic Performance

Preparation and Characterization of Mg(OH) 2 Nanorods by Liquid–solid Arc Discharge Technique

The Investigation on Preparation Technology of Nano-magnesia

Non-isothermal Decomposition Reaction Kinetics of the Magnesium Oxalate Dihydrate

Preparation of Nanometer NiO/MgO and Its Catalytic Performance for Thermal Decomposition of Ammonium Perchlorate

Non-isothermal kinetic study of high-grade magnesite thermal decomposition and morphological evolution of MgO