Calculation of Stress Intensity Factors of Surface Cracks Initiated from Repaired Welded Details under Bending Load

Xiao-yuan WU,Qiang LIU,Zi-li WANG,Ya-lin YUA,Xiao-ping HUANG,Wei-cheng CUI

DOI: https://doi.org/10.3969/j.issn.1007-7294.2007.05.010

2007-01-01

Abstract:It has been observed that fatigue cracks are prone to initiating from the stress concentration ar-eas such as the bottom of weld repaired profiles.When the surface crack has been found,the fatigue life should be evaluated in order to schedule the inspection period.In this paper,the stress intensity factors(SIFs) at the deepest point of the surface crack initiated from the bottom of the repaired profiles were cal-culated by finite element method based on linear elastic fracture mechanics(LEFM).To the repaired de-tails,the results show that SIFs will increase as the ratio of a/c decreases when the depth of the surface cracks was fixed.According to different weld repaired profiles,a group of empirical formulas were obtained by regressive method.It can be verified by the calculated results that the empirical formulas can be appli-cable to a certain range of details.According to empirical formulas based on LEFM,crack aspect ratio vari-ation of surface crack initiated from bottom of repaired profiles was investigated.With different aspect ratio from 1/2~1/5,the variation of increment ratio of minor and major half axis of semielliptical surface crack was obtained.Using specimens made of mild steel,experiments were carried out to study the crack aspect ratio variation under bending fatigue loading.The results indicate that the experimental points are consistent with calculated points from empirical formulas.The applicability of the empirical formulas was validated by comparison between experiments and finite element analyses.