Influences of Ti4+and Mg2+substitutions on the Properties of Lithium Ferrites

Hua Su,Huaiwu Zhang,Xiaoli Tang,Baoyuan Liu
DOI: https://doi.org/10.1088/1742-6596/152/1/012064
2009-01-01
Journal of Physics Conference Series
Abstract:The Ti4+ and Mg2+ co-substituted lithium ferrites with different compositions of Zn0.1Li0.45Mn0.1Fe2.35-2x (TiMg)xO4 (x=0.0-0.5) were prepared by the ceramic standard processing. The magnetic properties and microstructure of the samples were investigated. A single phase spinel structure was confirmed by XRD in substituting range. Sintering densities continuously decreased with the increase at x value, which was attributed to the fact that the heavier Fe3+ ions were replaced by the relatively lighter Ti4+ and Mg2+ ions. However, relative density of the samples had no obvious relationship with the substituting value. Saturation magnetization continuously decreased with x value, which was attributed to the decrease of resultant magnetic moment between A and B sub-lattice. Remanence decreased monotonously with x value due to the decrease of saturation magnetization and magnetocrystalline anisotropy constant. But the effect of Ti4+ and Mg2+ substitutions on the Br/Bs ratio values was not obvious. Coercive force was mainly determined by the microstructure and magnetocrystalline anisotropy constant of the ferrites. In this research, with the increase of Ti4+ and Mg2+ substitutions, the advantageous influence by the decrease of magnetocrystalline anisotropy constant was more significant than the disadvantageous influence caused by the increase of closed pores. As a result, coercive force of the ferrites also decreased monotonously with the increase at x value.
What problem does this paper attempt to address?