Effects of Ferrites on Magnetic Transport Properties in La2/3sr1/3mno3/Ferrites Composites

Zhengyou Zhou,Xiaoshan Wu,Jun Du,Sheng Xu,Xiaojun Bai,Guangsheng Luo,Fengyi Jiang

DOI: https://doi.org/10.1016/s1006-7191(08)60070-8

2009-01-01

Abstract:Effects of soft-magnetic MnZn ferrite (Mn0.5Zn0.5Fe2O4, MZF) and hard-magnetic Ba ferrite (BaO center dot 6Fe(2)O(3), BaM) on the structure and magnetic transport properties of [La2/3Sr1/3MnO3] (LSMO) /(x) [ferrites] (ferrites=MZF, BaM) composites have been investigated. It was found that the inclusion of MZF phase reduces magnetization and ferromagnetic-paramagnetic transition temperature (T-c) of the composites. With increasing the content of the dopants, the high-temperature magnetoresistance (MR) decreases, whereas low-temperature MR increases and reaches 42% at 150 K and x=0.1. However, for the LSMO/BaM composites, magnetization and ferromagnetic-paramagnetic transition temperature (T-c) decrease firstly as x<5%, and then increase as x>5%. The resistivity of the composites increases by five orders of magnitude at x=1% and is out of measured range at x=5%. High magnetic field has little effect on the resistivity and magnetoresistance for the composites with x>5%, which may originate from the pinning effect of BaM grains.