Improved mechanical response of Nano-SiO2 powder cemented soil under the coupling effect of dry and wet cycles and seawater corrosion
Qingsheng Chen,Shaozhen Wan,Gaoliang Tao,Zhihao Tian,Ronghu Yu,Sanjay Nimbalkar,Chen, Qingsheng,Wan, Shaozhen,Tao, Gaoliang,Tian, Zhihao,Yu, Ronghu
DOI: https://doi.org/10.1007/s11440-024-02237-8
2024-03-06
Acta Geotechnica
Abstract:The average salinity of seawater is 3.5%, with a significant presence of corrosive ions, primarily Cl − and SO 4 2− . In contrast to cement engineering in terrestrial natural environments, cement-reinforced structures exposed to corrosive marine environments not only endure ion erosion but also undergo periodic desiccation due to tidal variations in seawater. The coupling of these effects results in a reduction in the mechanical properties of cemented soil, inevitably leading to the degradation of cemented foundations, posing a serious threat to their safety and normal functionality. Investigating the improvement of the mechanical properties of cemented soil in corrosive coastal environments is a crucial engineering challenge in current coastal construction projects. To address this engineering challenge, this study proposes the use of Nano-SiO 2 to enhance the mechanical characteristics of cemented soil, aiming to improve the strength and durability of cement-reinforced structures. Simulating the main corrosive ions in seawater by using different concentrations of SO 4 2− ions, the study subjected cemented soil samples to dry–wet cycles to simulate the desiccation caused by tidal changes in seawater. Unconfined compressive strength tests were conducted on cemented soil and nano-cemented soil samples under coupled conditions, revealing that the incorporation of Nano-SiO 2 increased the strength of cemented soil and slowed down the corrosion rate. With an ion concentration of 12.3 g/L, after 60 dry and wet cycles, the compressive strength of nano-cemented soil increased by 90% compared to conventional cemented soil, with a mass loss only half that of conventional cemented soil. XRD, SEM, and NMR tests on various cemented soil samples indicated that the addition of Nano-SiO 2 filled small pores, suppressed pore development, and interacted with cement hydration products, forming a gel-like structure that improved the compactness of cemented soil. This, in turn, mitigated ion corrosion and the degradation of cemented soil under dry–wet cycles.
engineering, geological