Poly(Ester Urethane) Synthesized Via Chain Extension of Plla and Pbs Prepolymers Using Hdi

Zeng Jianbing,Li Yidong,Li Wenda,Zhu Qunying,Xiong Zhu,Yang Keke,Wang Yuzhong

DOI: https://doi.org/10.3724/sp.j.1105.2009.01018

2009-01-01

Acta Polymerica Sinica

Abstract:An aliphatic polyester,poly(butylene succinate)(PBS),which can be derived from renewable materials, was used to copolymerize with poly (L-lactic acid) (LPLA) through chain-extension reaction for preparing a biodegradable poly(ester urethane) (PEU). Hexamethylene diisocyanate (HDI) was used as a chain-extender. PLLA and PBS, having number-average molecular weight of 6350 g/mol and 10500 g/mol, respectively, were synthesized through condensation polymerization and were terminated with hydroxyl groups, which endowed them with high reactivity when reacting with isocyanate. The conditions for chain-extension reaction were optimized. It was found that the highest molecular weight. (MW) of PEU wits achieved when [NCO]/[OH] = 1 : 1, and the MW of PEU increased with the increase amount of PBS in the feed ratio. The structure and composition of PEU were characterized by (1)H-NMR. The molecular weight of PEU was determined by GPC, and the results indicated that the high molecular weight (say, M. of more 10(5) g/mol) can be easily achieved. The thermal and crystallization properties of PEU were investigated by DSC. The results suggested that the crystallization of PEU was mainly caused by PBS segments, and it was very difficult for PLLA segments to crystallize. In addition. the thermal stability of PEU was measured via TGA, and the results indicated that the degradation of PEU under went a two-stage process. PLLA segments degraded in the First stage and the PBS segments degraded in the second stage. Tensile properties of PEU were also studied. PEU with higher toughness than PLLA (say, an elongation at break of 323%) was obtained when the weight fraction of PBS reached 30%.