Abstract:The augmented finite element method (A-FEM) is used to study the fundamental composite failure problem of delamination and associated damage events spreading from a stress concentrator during tensile loading. The solution exploits the ability of A-FEM to account for coupled multiple crack types that are not predetermined in shape or number. The nonlinear processes of each fracture mode are represented by a cohesive model, which provides a unified description of crack initiation and propagation and can also describe crack coalescence and bifurcation. The study problem is an orthogonal double-notched tension specimen, in which delaminations interact with transverse ply cracks, intra-ply splitting cracks, non-localized fine-scale matrix shear deformation, and fiber breaks. Cohesive laws and constitutive laws for matrix shear deformation are calibrated using literature data from independent tests. The calibrated simulations are mesh independent and correctly reproduce all qualitative aspects of the coupled damage evolution processes. They also correctly predict delamination sizes and shapes, the density of transverse ply cracks, the growth rate of splitting cracks, softening of the global stress–strain curve, and the ultimate strength. A sensitivity analysis relates variability in cohesive law parameters to predicted deviance in engineering properties. Given the known variability in cohesive law parameters, the predicted deviance in ultimate strength agrees with that in experimental data. The importance of including the interactions between different crack systems and non-localized shear deformation is demonstrated by suppressing the presence of separate mechanisms; the predicted delamination shapes, splitting crack growth rate, and the stress–displacement relationship fall into significant error.

Study on composites delamination initiation and propagation criterion

Study on Mixed-Mode Interlaminar Fracture of Laminated Composites

Simulation of Delamination Propagation for Stiffened Composite Laminated Plates

Stress based fracture criteria for mixed-mode I/II delamination of unidirectional composite laminates

Nonlinear Fracture Analysis of Delamination Crack Jumps in Laminated Composites

Progress in Interfacial Mode Mixity of Laminated Composites

Delamination Analysis of Laminated Composites Based on Contact

Mode Mixity for Orthotropic Interface Delamination in Laminated Composites

On the Distribution of Delamination in Composite Structures and Compressive Strength Prediction for Laminates with Embedded Delaminations

Numerical Investigation on Behaviors of Composite Laminates with Initial Delamination Defects under Impact and Compression after Impact

Experimental and Numerical Analyses of Stiffened Composite Panels with Delamination under a Compressive Load

Characterization Methods of Delamination in a Plain Woven CFRP Composite

A comprehensive experimental investigation of the rate-dependent interlaminar delamination behaviour of CFRP composites

Application of a delamination model to laminated composite structures

XFEM Simulation of Delamination in Composite Laminates Part A Applied Science and Manufacturing

Simulation and analysis of delamination damage propagation in CFRP structures

In-situ Damage Mechanism Investigation and a Prediction Model for Delamination with Fibre Bridging in Composites

A delamination criterion for laminated composites under low-velocity impact

XFEM Simulation of Delamination in Composite Laminates

Fracture toughness and fiber bridging mechanism for mode-I interlaminar failure of spread-tow woven composites

High-fidelity Simulations of Multiple Fracture Processes in a Laminated Composite in Tension