Abstract:The development of effective catalytic systems for the synthesis of carbon nanomaterials by catalytic pyrolysis is a relevant direction for modern science. In this work, the peculiarities of the microdispersed alloy Ni 0.89 Cu 0.11 synthesis by mechanochemical alloying of metal powders in a planetary mill were investigated. The evolution of morphology and phase composition of Ni–Cu composite depending on the diameter of the milling balls and the activation time was studied using X-ray diffraction and particle size analyses, and scanning electron microscopy. The conditions corresponding to the formation of a single-phase Ni–Cu solid solution were determined and a scheme for the appearance of microdispersed alloy particles during the activation process was proposed. The prepared samples of the Ni–Cu composite were tested as catalyst precursors in the ethylene decomposition at 550 °C accompanied with the formation of carbon filaments. An extreme character of the carbon yield dependence on the activation time was found. The maximum carbon yield of 68–78 g/g cat after 15 min of reaction was achieved on the sample activated for 5–7 min and possessing slab morphology. The complete disintegration of the microdispersed Ni–Cu alloy was observed after ~ 1 min of a contact with the reaction medium. The resulting active particles were shown to catalyze the growth of carbon filaments. According to EDX data, the average content of copper in the composition of the active particles was estimated to be equal to its initial concentration in the alloy (~ 12 at.%).

Carbon Nanofiber Films Synthesized on Substrate with Copper Nanoparticles as Catalyst

Synthesis of Carbon Nanofiber Monoliths by Chemical Vapor Deposition

Growth of Carbon Nanofibers Catalyzed by Silica-Coated Copper Nanoparticles

Large-Scale and Selective Synthesis of Carbon Nanofiber Bundles, Curved Carbon Nanofibers and Helical Carbon Nanofibers.

Production of Carbon Nanofibers Using a CVD Method with Lithium Fluoride as a Supported Cobalt Catalyst

Morphology‐Controllable CVD Synthesis of Carbon Nanomaterials on an Alkali‐Element‐Doped Cu Catalyst.

Thermal CVD Synthesis of Carbon Nanotubes Filled with Single-Crystalline Cu Nanoneedles at Tips

Gas-induced formation of Cu nanoparticle as catalyst for high-purity straight and helical carbon nanofibers.

Preparation of high purity helical carbon nanofibers by the catalytic decomposition of acetylene and their growth mechanism

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD

Carbon Nanofibers: Synthesis, Characterization, and Electrochemical Properties

Synthesis of Copper-Core/Carbon-Sheath Nanocables by a Surfactant-Assisted Hydrothermal Reduction/Carbonization Process

Carbon Nanofiber Microspheres Obtained from Ethylene Using Fecl3 As the Catalyst Precursor

Kinetically Controlled Synthesis of Carbon Nanofibers with Different Morphologies by Catalytic CO Disproportionation over Iron Catalyst

Growth of Carbon Nanocoils Using Fe–Sn–O Catalyst Film Prepared by a Spin-Coating Method

Synthesis of carbon nanotubes and carbon onions by CVD using a Ni/Y catalyst supported on copper

Highly Efficient Synthesis of Carbon Nanocoils by Catalyst Particles Prepared by a Sol–gel Method

Large-Scale Synthesis of Herringbone Carbon Nanofibers on Nonsupported Nickel Catalyst

Synthesis of carbon nanofibers by CVD as a catalyst support material using atomically ordered Ni3C nanoparticles

Preparation of Ni–Cu Catalyst for Carbon Nanofiber Production by the Mechanochemical Route

Synthetic Hierarchical Nanostructures: Growth of Carbon Nanofibers on Microfibers by Chemical Vapor Deposition