Abstract:Carbon nanofibers (CNFs) were synthesized by CO disproportionation on iron catalyst at CO concentration between 58.3% and 75.0%, H2 concentration between 8.3% and 25.0% and reaction temperature between 833 and 913K. The time-depending rate of CNFs growth as a function of time was determined by an on-line mass spectrometer and the morphologies of all CNFs products were observed by electronic microscopy. Not only the CNFs growth rate but also the morphology of the grown CNFs were shown to vary with the three operating variables. SEM and TEM images showed that the three-dimensional morphologies of the CNFs were twist, helical or straight and an interesting relationship between the maximal growth rate and the morphology was observed. When the growth rate was between 0.8 and 0.9mmol/(sgcat), the CNFs were twist. As the growth rate increased to 1.0mmol/(sgcat), more helical nanofibers appeared. Straight nanofibers were produced when the growth rate reached the level of 1.2mmol/(sgcat). Finally when the rate of CNFs growth was high at 1.8mmol/(sgcat), the absolute majority of the solid products was amorphous carbon coexisting with some short and thick nanofibers. Under different operating conditions, the crystal faces of the catalysts had different anisotropy properties for carbon deposition, thus producing CNFs with different morphologies.

Growth of Carbon Nanofibers Catalyzed by Silica-Coated Copper Nanoparticles

Copper Catalyzing Growth of Single-Walled Carbon Nanotubes on Substrates

Growth of Carbon NanoStructures in Ceramic Materials

The Size Effect of Catalyst on the Growth of Helical Carbon Nanofibers

Preparation of high purity helical carbon nanofibers by the catalytic decomposition of acetylene and their growth mechanism

Gas-induced formation of Cu nanoparticle as catalyst for high-purity straight and helical carbon nanofibers.

Growth of High-Density Parallel Arrays of Ultralong Carbon Nanotubes with Catalysts Pinned by Silica Nanospheres

Carbon Nanotube Growth on the Surface of Carbon Fibers by CVD

Carbon Nanostructures Formed on Mesoporous Silica by Catalytic Chemical Vapor Deposition of Ethene

Carbon Nanofiber Films Synthesized on Substrate with Copper Nanoparticles as Catalyst

Synthesis of Helical and Straight Carbon Nanofibers on Water Soluble Sodium Chloride Supported Catalyst

In-situ Growth of Carbon Nano-tubes/Carbon Nano-fibers(CNTs/CNFs) on the Surface of Carbon Fibers and its Microstructure Investigation

Hexahedral nano-cementites catalysing the growth of carbon nanohelices

Iron Oxide Nanoparticle Impregnated Mesoporous Silicas As Platforms for the Growth of Carbon Nanotubes

Carbon fiber-promoted activation of catalyst for efficient growth of single-walled carbon nanotubes

Growth of Carbon Nanocoils Using Fe–Sn–O Catalyst Film Prepared by a Spin-Coating Method

Kinetically Controlled Synthesis of Carbon Nanofibers with Different Morphologies by Catalytic CO Disproportionation over Iron Catalyst

Growing pillars of densely packed carbon nanotubes on Ni-coated silica

Growth and Field Emission of Carbon Nanofibers on Electroless Ni-P Alloy Catalyst

Growth of High Quality, High Density Single-Walled Carbon Nanotube Forests on Copper Foils

Growth of Single-Walled Carbon Nanotubes from Discrete Catalytic Nanoparticles of Various Sizes