Abstract:The effect of composition tuning on glass forming ability (GFA), mechanical properties and atomic structure in ZrxCo84−xAl16 bulk metallic glasses (BMGs) with x = 51–58 has been investigated by using copper-mold suction casting, nanoindentation, high-energy X-ray diffraction, extended X-ray absorption fine structure experiments and ab initio molecular dynamics simulations, respectively. It is found that GFA firstly increases then decreases with increasing Zr content, exhibiting a maximum diameter of 7 mm with the Zr content of 55 and 56, while an abrupt reduction of bending plasticity occurs as the Zr content drops below 55. Both experimental and theoretical results find that GFA is remarkably enhanced, due to the abnormal reduction in the fractions of the Co-centered ⟨0, 2, 8, 1⟩, ⟨0, 3, 6, 2⟩ and ⟨0, 3, 6, 3⟩ polyhedra, and the denser atomic packing of Zr atoms around center Co atom, as the Zr content increases from 51 to 56. Meanwhile, the simultaneously improved plasticity is associated with the increased Co-centered ⟨0, 3, 6, 0⟩, and Al-centered ⟨0, 2, 8, 1⟩ and ⟨0, 3, 6, 2⟩ polyhedra, which provide more fertile sites for the nucleation of shear transformations. Further Zr addition to 58 increases remarkably the fractions of Zr- and Al-centered ⟨0, 1, 10, 2⟩ and ⟨0, 3, 6, 4⟩ polyhedra, and causes looser atomic packing of Co atoms around center Zr atom, leading to the reduction in GFA. However, the plasticity is not enhanced further but remains nearly constant, which may be related to the deteriorated effect on plasticity of the decreased fractions of Zr-centered ⟨0, 1, 10, 5⟩ and Co-centered ⟨0, 3, 6, 0⟩ polyhedra, and the increased fractions of Zr-centered ⟨0, 1, 10, 3⟩ and ⟨0, 2, 8, 4⟩ and Co-centered ⟨0, 2, 8, 0⟩ polyhedra. Compositional tuning, with internal structure tuned to favor both GFA and plastic flow, offers new possibilities in developing ductile BMG materials.

Enhanced Plasticity of a Zr50Cu48Al2 Bulk Metallic Glass

Thermophysical and Mechanical Properties of Multicomponent Zr37Hf16Ni12.5Cu12.5Al11Co6Nb5 Bulk Glass-Forming Alloy

Ultrasonic excitation induced nanocrystallization and toughening of Zr<sub>46.75</sub>Cu<sub>46.75</sub>Al<sub>6.5</sub> bulk metallic glass

Relating melting temperature with structure heterogeneity and plasticity of Zr57Cu20Al10Ni8Ag5 bulk metallic glass

Thermophysical and Mechanical Properties of Multicomponent Zr37Hf16Ni12.5Cu12.5Al1 1co6nb5 Bulk Glass-Forming Alloy

New Class of Plastic Bulk Metallic Glass.

Enhanced Plasticity by Introducing Icosahedral Medium-Range Order in Zrcunial Metallic Glass

Unusual Room Temperature Ductility of A Zr-Based Bulk Metallic Glass Containing Nanoparticles

Enhancement of Plasticity in Zr-based Bulk Metallic Glasses

Enhancing strength and plasticity of Zr-based bulk metallic glasses by Zr partially substituted Fe and isothermal annealing

A Plastic Zr–Cu–Ag–Al Bulk Metallic Glass

A Series of Zr-Based Bulk Metallic Glasses with Room Temperature Plasticity

Enhanced mechanical properties of Zr65Cu15Ni10Al10 bulk metallic glass by simultaneously introducing surface grooves and multiple shear bands

Enhanced Plasticity in a Zr-based Bulk Metallic Glass Containing Nanocrystalline Precipitates

Microalloying-induced Large Plasticity in La-Al-C Bulk Metallic Glass

Enhancement of Glass-Forming Ability and Plasticity Via Alloying the Elements Having Positive Heat of Mixing with Cu in Cu48Zr48Al4 Bulk Metallic Glass

Controlling the Mechanical Properties of Bulk Metallic Glasses by Superficial Dealloyed Layer

Substantially enhanced plasticity of bulk metallic glasses by densifying local atomic packing

Plasticity and microstructure of Zr–Cu–Al bulk metallic glasses

Glass forming ability and bending plasticity evolutions in Zr-Co-Al bulk metallic glasses and their structural origin

Mechanical Properties of Monolithic Zr62Al8Ni13Cu17 Bulk Metallic Glass