Abstract:Quasi-static monotonic, fatigue pre-crack initiation, and crack propagation tests were initially conducted on composite rock–concrete beams. Experimental results showed that during the fatigue pre-crack initiation, damage accumulated around the pre-crack tip, and its rate strongly depended on the upper fatigue load level S max and load ratio R . For the studied rock–concrete interface, the crack-mouth-opening displacement corresponding to the initial cracking load of monotonic test ( CMOD ini,m ) can be considered as a crack initiation criterion in the fatigue loading. Subsequently, a local stress-based fatigue damage evolution law involving S max and R was derived based on the concept of energetic equivalence from linear elastic fracture mechanics and continuum damage mechanics. This was followed by the simulation of fatigue pre-crack initiation for composite rock–concrete beam. The good agreement between the experimental and numerical results suggested that the combination of the derived damage evolution law and the CMOD ini,m -based crack initiation criterion can successfully simulate the fatigue pre-crack initiation of rock–concrete beam. The derived damage evolution law effectively characterized the local fatigue damage featured with microcracking. The numerical analysis of the damage distribution in the damage region around the pre-crack tip showed that S max greatly affected the rate of fatigue damage evolution, the total damage area, and damage distribution at the time of pre-crack initiation, whilst R primarily affected the rate of fatigue damage evolution and had a minor effect on the final damage results. Using the derived fatigue damage evolution law, the variation in structural stiffness during the initiation of preexisting interfacial cracks can be predicted under specific fatigue loading conditions, providing valuable guidance for load selection during design and operation.

Elastic–plastic finite element analysis and experimental study of short and long fatigue crack growth

Depth-sensing Indentation Measurement and Finite Element Analysis of Residual Stress Field Near Fatigue Crack Tip

The compressive stress effect on fatigue crack growth under tension–compression loading

An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

Finite Element Analysis of the Fatigue Crack Tip Parameters in the Glass Fiber Reinforced Aluminum Alloy Laminates under Tension-Compression Loading

Prediction of Low Cycle Fatigue Crack Growth under Mixed-mode Loading Conditions Using Cohesive Zone Models

Characterization of Crack-Tip Fields for Elastoplastic Fatigue Crack Growth Part I: Analysis of the ΔJ-integral

Experimental study of crack tip deformation under fatigue load

Evolution of a crack embedded in an elastic-plastic plate

Statistical Analysis Methods of Fatigue Crack Growth Rate

Experimental and Theoretical Study on Crack Growth Using Rock-Like Resin Samples Containing Inherent Fissures and its Numerical Assessment

Experimental studies on crack propagation and accumulative mean strain of cracked stiffened plates under low-cycle fatigue loads

A finite crack growth energy release rate for elastic-plastic fracture

Assessment of Crack-Tip Fields of Thermo-Mechanical Elastoplastic Fatigue Crack Growth

In-situ observation of strain evolution and ratchetting of growing fatigue cracks

Study of low-cycle fatigue crack growth behavior of central-cracked stiffened plates

Research on the Fatigue Crack Growth Behavior of a Zr/Ti/Steel Composite Plate with a Crack Normal to the Interface

Crack propagation behavior of different zones in weldment under creep-fatigue loadings

A computational approach to ductile crack growth under large scale yielding conditions

Short Fatigue-Crack Growth from Crack-like Defects under Completely Reversed Loading Predicted Based on Cyclic R-Curve

Investigation of Fatigue Crack Initiation of Rock–Concrete Interface Using a Stress-Based Fatigue Damage Evolution Law