Abstract:Retrogression and re-aging (RRA) treatment has been proven to effectively overcome the trade-off between strength and corrosion resistance. Current research focuses on the heating rate, temperature, and holding time of retrogression treatment while ignoring the retrogression cooling ways. In this paper, the effects of RRA treatment with different retrogression cooling ways on the microstructure and properties of newly developed T'/η' strengthened Al-Zn-Mg-Cu alloys were investigated by performing tests on mechanical properties, intergranular corrosion (IGC) resistance, and electrochemical corrosion behavior. The results show that the mechanical properties of samples subject to RRA treatment with water-quenching retrogression (ultimate tensile strength, yield strength, and elongation of 419.2 MPa, 370.2 MPa, and 15.9, respectively) are better than those of air-cooled and furnace-cooled samples. The corrosion resistance of water-quenching (IGC depth of 162.2 μm, corrosion current density of 0.833 × 10-5 A/cm2) and furnace-cooled samples (IGC depth of 123.7 μm, corrosion current density of 0.712 × 10-5 A/cm2) is better than that of air-cooled samples. Microstructure characterization reveals that the effect of the retrogression cooling rate on mechanical properties is related to the size of T'/η' precipitates with grains as well as the proportion of T' and η', while the difference in corrosion resistance depends on the continuity of grain boundary precipitates (GBPs). With mechanical properties, corrosion resistance, and time cost taken into consideration, it is appropriate to select water quenching for retrogression. These findings offer valuable insights for further design to achieve superior performance in various applications.

Small angle X-ray scattering study of the strengthen mechanism of Al–Mg–Li alloy during retrogression and reaging treatment

SAXS Investigation the Precipitation of Δ′ Phase in 1420 Alloy Treated by Aging-retrogression-reaging

Atomic-scale study on the precipitation behavior of an Al-Zn-Mg-Cu alloy during isochronal aging

Effect of continuous retrogression and re-ageing treatment on mechanical properties, corrosion behavior and microstructure of an Al-Zn-Mg-Cu alloy

Retrogression Characteristics of a Novel Al-Cu-Li-X Alloy

Effects of retrogression and re-aging treatment on precipitation behavior, mechanical and corrosion properties of a Zr+Er modified Al-Zn-Mg-Cu alloy

Small-angle X-Ray Scattering Study of the Formation and Growth of Δ' in Binary Al-7.87at% Li Alloy

Comprehensive improvement of stress corrosion cracking resistance and strength by retrogression and re-aging in Al-8.9Zn-2.6Mg-1.7Cu alloy

Effect of retrograssion and re-aging on microstructure and properties of Al–Zn–Mg–Cu–Zr–Er alloy

Effect of retrogression treatments on microstructure, hardness and corrosion behaviors of aluminum alloy 7085

Enhanced Fatigue Crack Propagation Resistance in an Al-Zn-Mg-Cu Alloy by Retrogression and Reaging Treatment

Microstructure Evolution and In Situ Resistivity Response of 2196 Al−Li Alloy during Aging Process

Precipitation behavior during re-aging of Al-Mg-Si-Cu alloy

Revealing the mechanisms of exfoliation corrosion and stress corrosion cracking for an Al-Zn-Mg-Cu alloy after continuous retrogression and re-ageing treatment

Microstructural evolution, precipitation behavior and mechanical properties of a novel Al–Zn–Mg–Cu–Li–Sc–Zr alloy

Effect of Retrogression with Different Cooling Ways on the Microstructure and Properties of T'/η' Strengthened Al-Zn-Mg-Cu Alloys

Precipitation behavior and properties of extruded 7136 aluminum alloy under different aging treatments

Precipitation behavior of an Al–Cu–Li–X alloy and competing relationships among precipitates at different aging temperatures

Microstructure evolution and recrystallization kinetics of Al-Cu-Li alloy during thermo-mechanical treatment with overaging and electrically-assisted annealing

Effect of Various Retrogression Regimes on Aging Behavior and Precipitates Characterization of a High Zn-Containing Al–Zn–Mg–Cu Alloy

Effect of ageing time on strength and microstructures of an Al–Cu–Li–Zn–Mg–Mn–Zr alloy